CAJ | 학술논문

采用电刷镀技术制备了Ni／ZrO2纳米复合镀层。利用扫描电子显微镜、X射线衍射等手段，研究了Ni／ZrO2纳米复合刷镀层的组织和抗高温氧化性能，并与快速镍镀层进行对比分析。结果表明，与快速镍镀层相比，Ni／ZrO2纳米复合镀层的表面形貌更为平整致密，晶粒尺寸明显减小；在800℃氧化后复合镀层晶粒依然较快速镍镀层细小、均匀，氧化增重速率明显低于快速镍镀层；X射线衍射分析表明，Ni／ZrO2复合镀层的氧化程度较轻，镀层中仍然存在大量的Ni相。
채용전쇄도기술제비료Ni／ZrO2납미복합도층。이용소묘전자현미경、X사선연사등수단，연구료Ni／ZrO2납미복합쇄도층적조직화항고온양화성능，병여쾌속얼도층진행대비분석。결과표명，여쾌속얼도층상비，Ni／ZrO2납미복합도층적표면형모경위평정치밀，정립척촌명현감소；재800℃양화후복합도층정립의연교쾌속얼도층세소、균균，양화증중속솔명현저우쾌속얼도층；X사선연사분석표명，Ni／ZrO2복합도층적양화정도교경，도층중잉연존재대량적Ni상。
Nickel based composite coating with nano-ZrO2 particles was prepared by electro-brush plating. The microstructure and high temperature oxidation resistance of Ni/ZrO2 composite coating were studied with scan electronic microscope and X-ray diffraction compared with fast nickel coating. The results show that the surface morphology of Ni/ZrO2 nano composite coating was relatively smooth and compact and the crystal size obvious reduced. High-temperature oxidation test in air at 800℃ indicates that the grain size of Ni/ZrO2 nano composite coating after oxidation is still smaller and more evenly and the weight-increased rate is obviously lower than that of fast nickel coating. The XRD analysis shows that oxidation degree of Ni/ZrO2 composite coatings is lighter, and there are a lot of nickel phases.