目的制备聚己内酯(PCL)长效药物缓释制剂,优化药物缓释效果,并研究PCL埋植剂的药物通透性.方法 合成分子质量为(8~16)×104 u含有普朗尼克F68的PCL,用挤出法制备不同壁厚的PCL长效缓释埋植剂.将左炔诺孕酮(LNG)装入PCL管封装,制成LNG药囊.通过高效液相色谱法测定LNG的释放效果,考察PCL的分子质量及PCL管壁厚度对LNG通透性的影响.结果 当PCL分子质量为(8~16)×104u时,对LNG通透性无显著影响.PCL管壁厚在0.20~0.40 mm时,对LNG通透性亦无显著影响;当壁厚小于0.15 mm时,LNG通透性显著提高.结论 PCL埋植剂对LNG具有通透性,可通过改变PCL管壁厚度增加药物通透性.
目的製備聚己內酯(PCL)長效藥物緩釋製劑,優化藥物緩釋效果,併研究PCL埋植劑的藥物通透性.方法 閤成分子質量為(8~16)×104 u含有普朗尼剋F68的PCL,用擠齣法製備不同壁厚的PCL長效緩釋埋植劑.將左炔諾孕酮(LNG)裝入PCL管封裝,製成LNG藥囊.通過高效液相色譜法測定LNG的釋放效果,攷察PCL的分子質量及PCL管壁厚度對LNG通透性的影響.結果 噹PCL分子質量為(8~16)×104u時,對LNG通透性無顯著影響.PCL管壁厚在0.20~0.40 mm時,對LNG通透性亦無顯著影響;噹壁厚小于0.15 mm時,LNG通透性顯著提高.結論 PCL埋植劑對LNG具有通透性,可通過改變PCL管壁厚度增加藥物通透性.
목적제비취기내지(PCL)장효약물완석제제,우화약물완석효과,병연구PCL매식제적약물통투성.방법 합성분자질량위(8~16)×104 u함유보랑니극F68적PCL,용제출법제비불동벽후적PCL장효완석매식제.장좌결낙잉동(LNG)장입PCL관봉장,제성LNG약낭.통과고효액상색보법측정LNG적석방효과,고찰PCL적분자질량급PCL관벽후도대LNG통투성적영향.결과 당PCL분자질량위(8~16)×104u시,대LNG통투성무현저영향.PCL관벽후재0.20~0.40 mm시,대LNG통투성역무현저영향;당벽후소우0.15 mm시,LNG통투성현저제고.결론 PCL매식제대LNG구유통투성,가통과개변PCL관벽후도증가약물통투성.
Objective To prepare polycaprolactone (PCL) implant with long-term sustained release,optimize the drug delivery effect and observe the permeability of PCL for drug.Methods PCL implant with average molecular weight of (8-16)×104 u were synthesized and extruded into tubes.The tubular capsules were filled with levonorgestrel (LNG),closed at both ends.The drug release of PCL implant was measured by HPLC.The drug permeability of PCL implant was evaluated with different molecular weight and thickness.Results The molecular weight of (8-16)×104 u showed no effect on the permeability of PCL implant for LNG.The thickness of 0.20-0.40 mm of PCL membranes showed no effect on the permeability for LNG.The PCL membranes with the thickness of less than 0.15 mm had the higher permeability than those with the thickness of 0.20-0.40 mm.Conclusions The PCL implant is permeable for LNG and the permeability can be increased by decreasing the thickness of membrane.