中华口腔医学杂志
中華口腔醫學雜誌
중화구강의학잡지
Chinese Journal of Stomatology
2012年
9期
538-541
,共4页
马洪学%申丽丽%刘琨%苏林旺
馬洪學%申麗麗%劉琨%囌林旺
마홍학%신려려%류곤%소림왕
显微镜检查,电子,扫描%牙本质粘结剂%根管充填材料%玻璃纤维桩
顯微鏡檢查,電子,掃描%牙本質粘結劑%根管充填材料%玻璃纖維樁
현미경검사,전자,소묘%아본질점결제%근관충전재료%파리섬유장
Microscopy,electron, scanning%Dentin-bonding agents%Root canal filling materials%Glass fiber post
目的 观察不同根管封闭材料和不同粘接程序对纤维桩树脂粘接后牙本质粘接界面微观结构的影响,以期改进临床操作步骤,优化纤维桩的树脂粘接效果.方法 选择15颗人下颌单根第一前磨牙,分为5组,每组3颗:A组:氧化锌丁香油糊剂根充,常规粘接纤维桩( Relyx Unicem);B组:Vitapex封闭剂根充,常规粘接纤维桩;C~E组:AH Plus封闭剂根充,C组常规粘接纤维桩,D组35%磷酸酸蚀+常规粘接纤维桩,E组酸蚀后涂布Singlebond2粘接剂+常规粘接纤维桩.将牙根浸于生理盐水中1周后截为根冠1/3、根中1/3、根尖1/3段,每段厚3 mm.扫描电镜观察.结果 除D组外,A、B、C、E组牙本质粘接界面均出现树脂突.每种根管封闭剂根冠1/3段树脂突最多、最明显,其次是根中1/3段,根尖1/3段最不明显.不同组牙根中自粘接树脂形成树脂突的情况不同.A和B组仅根冠1/3段出现较少的树脂突,C~E组根中1/3段和根冠1/3段均出现较多的树脂突.与C组相比,增加酸蚀步骤的D组未见明显树脂突形成,而酸蚀后涂布粘接剂的E组牙根内树脂突增大伸长更加明显.结论 对于使用纤维桩加强的残根残冠,建议使用C~E组根管封闭剂,无需在纤维桩粘接程序前进行酸蚀处理,而酸蚀后涂布粘接剂有可能增加纤维桩的粘固力.
目的 觀察不同根管封閉材料和不同粘接程序對纖維樁樹脂粘接後牙本質粘接界麵微觀結構的影響,以期改進臨床操作步驟,優化纖維樁的樹脂粘接效果.方法 選擇15顆人下頜單根第一前磨牙,分為5組,每組3顆:A組:氧化鋅丁香油糊劑根充,常規粘接纖維樁( Relyx Unicem);B組:Vitapex封閉劑根充,常規粘接纖維樁;C~E組:AH Plus封閉劑根充,C組常規粘接纖維樁,D組35%燐痠痠蝕+常規粘接纖維樁,E組痠蝕後塗佈Singlebond2粘接劑+常規粘接纖維樁.將牙根浸于生理鹽水中1週後截為根冠1/3、根中1/3、根尖1/3段,每段厚3 mm.掃描電鏡觀察.結果 除D組外,A、B、C、E組牙本質粘接界麵均齣現樹脂突.每種根管封閉劑根冠1/3段樹脂突最多、最明顯,其次是根中1/3段,根尖1/3段最不明顯.不同組牙根中自粘接樹脂形成樹脂突的情況不同.A和B組僅根冠1/3段齣現較少的樹脂突,C~E組根中1/3段和根冠1/3段均齣現較多的樹脂突.與C組相比,增加痠蝕步驟的D組未見明顯樹脂突形成,而痠蝕後塗佈粘接劑的E組牙根內樹脂突增大伸長更加明顯.結論 對于使用纖維樁加彊的殘根殘冠,建議使用C~E組根管封閉劑,無需在纖維樁粘接程序前進行痠蝕處理,而痠蝕後塗佈粘接劑有可能增加纖維樁的粘固力.
목적 관찰불동근관봉폐재료화불동점접정서대섬유장수지점접후아본질점접계면미관결구적영향,이기개진림상조작보취,우화섬유장적수지점접효과.방법 선택15과인하합단근제일전마아,분위5조,매조3과:A조:양화자정향유호제근충,상규점접섬유장( Relyx Unicem);B조:Vitapex봉폐제근충,상규점접섬유장;C~E조:AH Plus봉폐제근충,C조상규점접섬유장,D조35%린산산식+상규점접섬유장,E조산식후도포Singlebond2점접제+상규점접섬유장.장아근침우생리염수중1주후절위근관1/3、근중1/3、근첨1/3단,매단후3 mm.소묘전경관찰.결과 제D조외,A、B、C、E조아본질점접계면균출현수지돌.매충근관봉폐제근관1/3단수지돌최다、최명현,기차시근중1/3단,근첨1/3단최불명현.불동조아근중자점접수지형성수지돌적정황불동.A화B조부근관1/3단출현교소적수지돌,C~E조근중1/3단화근관1/3단균출현교다적수지돌.여C조상비,증가산식보취적D조미견명현수지돌형성,이산식후도포점접제적E조아근내수지돌증대신장경가명현.결론 대우사용섬유장가강적잔근잔관,건의사용C~E조근관봉폐제,무수재섬유장점접정서전진행산식처리,이산식후도포점접제유가능증가섬유장적점고력.
Objective To observe the influence of different bonding process and three different root canal sealing materials on microstructure of root canal dentin bonding interface after fiber post and resin bonding,so as to improve clinical operation steps and to optimize fiber post resin bonding effect. Methods Fifteen human single mandibular first premolars were selected.Three were bonded with fiber posts through Relyx Unicem conventional bonding steps after filled with root canal sealing materials of zinc oxide eugenol paste( Group A),and another three were bonded through the same steps after filled with sealing materials of Vitapex(Group B). The other nine were filled with sealing materials of AH Plus,randomly divided into three groups and bonded through different steps as follows:conventional bonding steps only ( Group C ),etching with 35% phosphoric acid before conventional bonding steps (Group D),and etching and coating with Singlebond 2 adhesive before conventional bonding steps( Group E).After immersed in saline solution for one week,all the roots were cut into three sections of 3 mm in thickness with emery chip and numbered as crown section,middle section and tip section respectively.The samples were observed the resin protrusion in mixed layer of dentin interface and dentinal tubules by scanning electron microscopy. Results We observed the resin protrusion in microstructures of the roots bonded through Relyx Unicem after filled with three different root canal sealing materials(Group A,B,C,E):most obvious in the root crown sections,middle in the root middle sections and least in the root tip sections.Differences were observed in roots filled with different sealing materials:little resin protrusion were observed in crown sections only in Group A and B,but large number of resin protrusion were found in crown and middle sections in Group C-E.Compared with Group C,no more resin protrusion were found in Group D.More and elongated resin protrusions were found in Group E.Conclusions We recommend using AH Plus as root canal sealing materials for residual crown and root needed to strengthen by fiber post. It is no need to etch before Relyx Unicem conventional bonding steps.However,coating Singlebond 2 adhesive after acid etching has the potential to increase fiber post cementation.