Tooth,deciduous%Dental caries%Composite resins%Dental cements
目的 比较渗透树脂和粘接剂在乳磨牙邻面早期龋损中的渗透能力,以期为渗透树脂在乳牙龋中的应用提供依据.方法 选取32颗邻面呈白垩色改变的早期龋损离体乳磨牙,垂直于白垩色斑块表面将牙齿切开,在体视显微镜下进行病损组织学分级(C1~C4):C1:龋损位于釉质外1/2;C2:龋损位于釉质内1/2;C3:龋损位于牙本质外1/2;C4:龋损延伸至牙本质内1/2.随后病损用15%的盐酸酸蚀2 min后,分别用渗透树脂(渗透树脂组)和粘接剂(粘接剂组)渗透5 min.使用激光扫描共聚焦显微镜在双荧光模式下观察,分别测量病损深度及渗透树脂和粘接剂的渗透深度,并计算渗透百分数.两组间比较使用配对符号秩和检验,同组不同组织学病损分级间比较使用多样本秩和检验.结果 所有样本病损组织学分级为C1~C3级,渗透树脂组与粘接剂组C1、C2、C3级的渗透深度分别为240(230,260)和190(150,210) μm、405(300,523)和180(160,200) μm、590(430,640)和180(160,200) μm,同组织学分级的两组差异有统计学意义(P<0.05);渗透树脂组各级渗透深度差异有统计学意义(P<0.01).渗透树脂组C1~C3级的渗透百分数分别为[100.0%(96.2%,100.0%)]、[99.1%(95.7%,100.0%)]、[82.0%(81.1%,92.2%)],粘接剂组C1 ~ C3级的渗透百分数分别为[79.2%(68.4%,87.5%)]、[41.8%(29.1%,74.5%)]、[30.2% (29.2%,39.6%)],同组织学分级的两组差异有统计学意义(P<0.05);渗透树脂组C3级渗透百分数与C1、C2级差异有统计学意义(P<0.05).结论 渗透树脂能有效地,甚至完全渗入乳磨牙邻面早期非洞龋损中.
目的 比較滲透樹脂和粘接劑在乳磨牙鄰麵早期齲損中的滲透能力,以期為滲透樹脂在乳牙齲中的應用提供依據.方法 選取32顆鄰麵呈白堊色改變的早期齲損離體乳磨牙,垂直于白堊色斑塊錶麵將牙齒切開,在體視顯微鏡下進行病損組織學分級(C1~C4):C1:齲損位于釉質外1/2;C2:齲損位于釉質內1/2;C3:齲損位于牙本質外1/2;C4:齲損延伸至牙本質內1/2.隨後病損用15%的鹽痠痠蝕2 min後,分彆用滲透樹脂(滲透樹脂組)和粘接劑(粘接劑組)滲透5 min.使用激光掃描共聚焦顯微鏡在雙熒光模式下觀察,分彆測量病損深度及滲透樹脂和粘接劑的滲透深度,併計算滲透百分數.兩組間比較使用配對符號秩和檢驗,同組不同組織學病損分級間比較使用多樣本秩和檢驗.結果 所有樣本病損組織學分級為C1~C3級,滲透樹脂組與粘接劑組C1、C2、C3級的滲透深度分彆為240(230,260)和190(150,210) μm、405(300,523)和180(160,200) μm、590(430,640)和180(160,200) μm,同組織學分級的兩組差異有統計學意義(P<0.05);滲透樹脂組各級滲透深度差異有統計學意義(P<0.01).滲透樹脂組C1~C3級的滲透百分數分彆為[100.0%(96.2%,100.0%)]、[99.1%(95.7%,100.0%)]、[82.0%(81.1%,92.2%)],粘接劑組C1 ~ C3級的滲透百分數分彆為[79.2%(68.4%,87.5%)]、[41.8%(29.1%,74.5%)]、[30.2% (29.2%,39.6%)],同組織學分級的兩組差異有統計學意義(P<0.05);滲透樹脂組C3級滲透百分數與C1、C2級差異有統計學意義(P<0.05).結論 滲透樹脂能有效地,甚至完全滲入乳磨牙鄰麵早期非洞齲損中.
목적 비교삼투수지화점접제재유마아린면조기우손중적삼투능력,이기위삼투수지재유아우중적응용제공의거.방법 선취32과린면정백성색개변적조기우손리체유마아,수직우백성색반괴표면장아치절개,재체시현미경하진행병손조직학분급(C1~C4):C1:우손위우유질외1/2;C2:우손위우유질내1/2;C3:우손위우아본질외1/2;C4:우손연신지아본질내1/2.수후병손용15%적염산산식2 min후,분별용삼투수지(삼투수지조)화점접제(점접제조)삼투5 min.사용격광소묘공취초현미경재쌍형광모식하관찰,분별측량병손심도급삼투수지화점접제적삼투심도,병계산삼투백분수.량조간비교사용배대부호질화검험,동조불동조직학병손분급간비교사용다양본질화검험.결과 소유양본병손조직학분급위C1~C3급,삼투수지조여점접제조C1、C2、C3급적삼투심도분별위240(230,260)화190(150,210) μm、405(300,523)화180(160,200) μm、590(430,640)화180(160,200) μm,동조직학분급적량조차이유통계학의의(P<0.05);삼투수지조각급삼투심도차이유통계학의의(P<0.01).삼투수지조C1~C3급적삼투백분수분별위[100.0%(96.2%,100.0%)]、[99.1%(95.7%,100.0%)]、[82.0%(81.1%,92.2%)],점접제조C1 ~ C3급적삼투백분수분별위[79.2%(68.4%,87.5%)]、[41.8%(29.1%,74.5%)]、[30.2% (29.2%,39.6%)],동조직학분급적량조차이유통계학의의(P<0.05);삼투수지조C3급삼투백분수여C1、C2급차이유통계학의의(P<0.05).결론 삼투수지능유효지,심지완전삼입유마아린면조기비동우손중.
Objective To compare the penetration abilities of resin infiltration into proximal lesions in primary molars with those of adhesive in vitro.Methods Thirty-two extracted or exfoliated primary molars showing proximal white spot lesions were selected.Roots of the teeth were removed,and the crowns were cut across the white spot lesions perpendicular to the surface.Cut surfaces were examined (by stereo microscopy) and classified with respect to histological lesion extension (C1-C4):lesions confined to the outer half on enamel(C1),lesions confined to the inner half on enamel(C2),lesions confined to the outer half on dentin(C3),lesions extending into the inner half of dentin (C4).Corresponding lesion halves were etched for 120 s with 15% hydrochloric acid gel and were subsequently treated with either adhesive or resin infiltration.Specimens were observed with laser scanning confocal microscope(LSCM) in dual fluorescence mode.In confocal microscopic images,lesion depth and penetration depth of the resin infiltration or the adhesive in corresponding halves were measured,and penetration percentages were calculated respectively.Differences of the data between two groups were analyzed by Wilcoxon signed rank test.Variations of histological caries extensions were detected with Kruskal-Wallis H test.Results At the same grading level (C1-C3) in histological caries extension,penetration depths of the resin infiltration group and the adhesive group were 240(230,260) μm vs 190(150,210) μm,405(300,523) μm vs 180(160,200) μm,and 590(430,640) μm vs 180(160,200) μm respectively.There was significant statistical difference in the data between two groups (P<0.05).Statistically significant difference in penetration depths of the resin infiltration group (at C1-C3) were found (P < 0.01).At the same grading level (C1-C3) in histological caries extension,percentage penetrations of the resin infiltration group and the adhesive group were [100.0% (96.2%,100.0%)],[99.1% (95.7%,100.0%)],[82.0% (81.1%,92.2%)] and [79.2% (68.4%,87.5%)],[41.8% (29.1%,74.5%)],[30.2% (29.2%,39.6%)],respectively.The difference between the above data was also significant(P < 0.05).Percentage penetrations of the resin infiltration group at C1 and C2 level was higher than those at C3 level(P < 0.05).Conclusions The resin infiltration is capable of penetrating almost completely into proximal lesions in primary molars.