目的 评价人工老化后瓷聚体-树脂水门汀联合体的颜色稳定性,为临床合理选择和应用瓷聚体贴面提供参考.方法 3种厚度(1.00、0.75、0.50 mm)瓷聚体(Ceramage)分别与5种色调[A1、A3、B0.5、WO(白色不透明)、TR(透明)]树脂水门汀(RelyX Veneer)制备瓷聚体-树脂水门汀联合体样本,共15组(每组5个样本),作为实验组.以3种厚度(1.00、0.75、0.50 mm)瓷聚体样本作为3个对照组(每组5个样本).所有样本同时放入氙灯老化仪中进行人工加速老化,分光光度仪测量老化前后样本的明度(L*)、红绿色品(a*)和黄蓝色品(b*)值,计算老化前后明度变化(△L)、红绿色品变化(△a)、黄蓝色品变化(△b)和色差(△E).用方差分析探讨瓷聚体厚度和树脂水门汀色调对老化前后△E的影响.结果 不同厚度瓷聚体或不同色调水门汀对瓷聚体-树脂水门汀联合体老化前后△E有影响(P<0.05),且瓷聚体厚度和水门汀色调间存在交互作用(P<0.05).所有实验组△E均小于3.3.所有实验组老化后L*均降低,且△L均小于2.0.结论 瓷聚体厚度与树脂水门汀色调均对瓷聚体-树脂水门汀联合体的颜色稳定性有影响;瓷聚体-树脂水门汀联合体老化后的明度变化和色差均在临床可接受的范围内.
目的 評價人工老化後瓷聚體-樹脂水門汀聯閤體的顏色穩定性,為臨床閤理選擇和應用瓷聚體貼麵提供參攷.方法 3種厚度(1.00、0.75、0.50 mm)瓷聚體(Ceramage)分彆與5種色調[A1、A3、B0.5、WO(白色不透明)、TR(透明)]樹脂水門汀(RelyX Veneer)製備瓷聚體-樹脂水門汀聯閤體樣本,共15組(每組5箇樣本),作為實驗組.以3種厚度(1.00、0.75、0.50 mm)瓷聚體樣本作為3箇對照組(每組5箇樣本).所有樣本同時放入氙燈老化儀中進行人工加速老化,分光光度儀測量老化前後樣本的明度(L*)、紅綠色品(a*)和黃藍色品(b*)值,計算老化前後明度變化(△L)、紅綠色品變化(△a)、黃藍色品變化(△b)和色差(△E).用方差分析探討瓷聚體厚度和樹脂水門汀色調對老化前後△E的影響.結果 不同厚度瓷聚體或不同色調水門汀對瓷聚體-樹脂水門汀聯閤體老化前後△E有影響(P<0.05),且瓷聚體厚度和水門汀色調間存在交互作用(P<0.05).所有實驗組△E均小于3.3.所有實驗組老化後L*均降低,且△L均小于2.0.結論 瓷聚體厚度與樹脂水門汀色調均對瓷聚體-樹脂水門汀聯閤體的顏色穩定性有影響;瓷聚體-樹脂水門汀聯閤體老化後的明度變化和色差均在臨床可接受的範圍內.
목적 평개인공노화후자취체-수지수문정연합체적안색은정성,위림상합리선택화응용자취체첩면제공삼고.방법 3충후도(1.00、0.75、0.50 mm)자취체(Ceramage)분별여5충색조[A1、A3、B0.5、WO(백색불투명)、TR(투명)]수지수문정(RelyX Veneer)제비자취체-수지수문정연합체양본,공15조(매조5개양본),작위실험조.이3충후도(1.00、0.75、0.50 mm)자취체양본작위3개대조조(매조5개양본).소유양본동시방입선등노화의중진행인공가속노화,분광광도의측량노화전후양본적명도(L*)、홍록색품(a*)화황람색품(b*)치,계산노화전후명도변화(△L)、홍록색품변화(△a)、황람색품변화(△b)화색차(△E).용방차분석탐토자취체후도화수지수문정색조대노화전후△E적영향.결과 불동후도자취체혹불동색조수문정대자취체-수지수문정연합체노화전후△E유영향(P<0.05),차자취체후도화수문정색조간존재교호작용(P<0.05).소유실험조△E균소우3.3.소유실험조노화후L*균강저,차△L균소우2.0.결론 자취체후도여수지수문정색조균대자취체-수지수문정연합체적안색은정성유영향;자취체-수지수문정연합체노화후적명도변화화색차균재림상가접수적범위내.
Objective To investigate the color stability of ceromer veneers/resin cements after accelerated ageing,and to provide the reference for clinical application and choice.Methods Fifteen groups of ceromer veneers/resin cements samples,five samples in each group,were prepared as experimental groups.In the fifteen groups,ceromer veneers in three thickness (1.00,0.75,0.50 mm) and resin cements of five shades(A1,A3,B 0.5,WO,TR),were matched through permutation and combination.Three groups of ceromer veneers with different thickness (1.00,0.75,0.50 mm) were used as control groups.All samples were put into xenon lamp ageing instrument to accelerate ageing.Spectrophotometer were used to measure the lightness(L*),red green color(a*) and blue yellow color(b*) of samples before and after accelerated ageing process,and the change of lightness (△L),red green color (△a),blue yellow color (△b) and color variation(△E) were calctlated.We investigated the effect of thickness of ceromer veneer and color of resin cement on color variation by using analysis of variance.Results The thickness factor and color factor showed significant effect on △E values,and they have interaction (P <0.05).The △E values of all experimental groups were lower than 3.3.After accelerated ageing,all L* values of experimental groups decreased,and △L values were lower than 2.0.Conclusions The thickness of ceromer veneer and the color of resin cement could both affect the color stability of ceromer veneers/resin cements.The changes of lightness and color in ceromer veneers/resin cements were considered clinically acceptable after accelerated ageing.