物理学报
物理學報
물이학보
2013年
6期
470-474
,共5页
郭春生?%万宁%马卫东%张燕峰%熊聪%冯士维
郭春生?%萬寧%馬衛東%張燕峰%熊聰%馮士維
곽춘생?%만저%마위동%장연봉%웅총%풍사유
失效机理一致性%恒定温度应力加速实验%威布尔分布
失效機理一緻性%恆定溫度應力加速實驗%威佈爾分佈
실효궤리일치성%항정온도응력가속실험%위포이분포
failure mechanism consistency%constant temperature stress accelerated test%Weibull distribution
针对加速实验中因失效机理发生改变而导致的无效实验问题,对失效机理一致性和分别在不同应力下器件的初期退化参数分布的关系进行了研究.研究证明了判断加速实验失效机理一致的条件:1)不同应力下失效分布的形状参数服从一致,即mi=m, i=1,2,3,···,2)尺度参数ηi服从ηi=AFi ·η.从而提供一种在实验初期即可根据参数退化分布快速判别不同应力下失效机理是否一致的方法,避免了因失效机理发生改变而造成的无效加速实验.最后对加速实验初期理论退化数据和多芯片组件厚膜电阻初期退化数据进行了威布尔分布参数估计,并对其在不同应力下的失效机理一致性进行了判别.
針對加速實驗中因失效機理髮生改變而導緻的無效實驗問題,對失效機理一緻性和分彆在不同應力下器件的初期退化參數分佈的關繫進行瞭研究.研究證明瞭判斷加速實驗失效機理一緻的條件:1)不同應力下失效分佈的形狀參數服從一緻,即mi=m, i=1,2,3,···,2)呎度參數ηi服從ηi=AFi ·η.從而提供一種在實驗初期即可根據參數退化分佈快速判彆不同應力下失效機理是否一緻的方法,避免瞭因失效機理髮生改變而造成的無效加速實驗.最後對加速實驗初期理論退化數據和多芯片組件厚膜電阻初期退化數據進行瞭威佈爾分佈參數估計,併對其在不同應力下的失效機理一緻性進行瞭判彆.
침대가속실험중인실효궤리발생개변이도치적무효실험문제,대실효궤리일치성화분별재불동응력하기건적초기퇴화삼수분포적관계진행료연구.연구증명료판단가속실험실효궤리일치적조건:1)불동응력하실효분포적형상삼수복종일치,즉mi=m, i=1,2,3,···,2)척도삼수ηi복종ηi=AFi ·η.종이제공일충재실험초기즉가근거삼수퇴화분포쾌속판별불동응력하실효궤리시부일치적방법,피면료인실효궤리발생개변이조성적무효가속실험.최후대가속실험초기이론퇴화수거화다심편조건후막전조초기퇴화수거진행료위포이분포삼수고계,병대기재불동응력하적실효궤리일치성진행료판별.
@@@@For avoiding the invalid acceleration experiments caused by the changes of the failure mechanism, the relationship of the failure mechanism consistency and the parameters of degradation data distribution in the early stage under different accelerated stress levels has been derived. Conditions for judging the failure mechanism consistency are also given as follows: firstly, the shape parameters of failure distribution has a uniform distribution mi=m, i=1,2,3,···; secondly, the dimension parameterηi follows the equationηi=AFi ·η. A method to rapidly discriminate the consistency of failure mechanism under different experimental stresses in the early stage was obtained, and the invalid acceleration experiments caused by the changes of the failure mechanism could be avoided. Finally, theoretical degenerate data in the early stage of the accelerated test and the initial degenerate data of the MCM thick-film resistor were used for estimating, Weibull distribution parameter, and the consistency of failure mechanism degradation was also judged.