王春红%白肃跃%马海军%岳鑫敏%吴美雅%于飞
王春紅%白肅躍%馬海軍%嶽鑫敏%吳美雅%于飛
왕춘홍%백숙약%마해군%악흠민%오미아%우비
纤维%提取%优化%乌拉草纤维%多指标正交分析%保暖性%抗菌性
纖維%提取%優化%烏拉草纖維%多指標正交分析%保暖性%抗菌性
섬유%제취%우화%오랍초섬유%다지표정교분석%보난성%항균성
fibers%extraction%optimization%curaua fiber%multiple indicator orthogonal analysis%adiathermic%antibacterial
为了提取一种新型植物纤维-乌拉草纤维并研究其性能,采用超声波-碱氧-浴法从乌拉草秸秆中提取乌拉草纤维,用多指标正交试验方法对超声波时间,碱煮时间,碱用量和双氧水用量进行优化设计,并通过对直径,断裂强度,回潮率3个指标的综合分析评价确定最佳提取工艺,对处理后的乌拉草纤维进行基本性能测试及保暖、抗菌效果测试.结果表明:最佳工艺参数为:超声波时间为70 min;碱氧-浴时间为100 min;0.75 L溶液中碱质量浓度为8 g/L;双氧水质量浓度为12 g/L.采用最优工艺所提取的乌拉草纤维平均直径、长度、断裂强度及回潮率分别为47.19μm、152.59 mm、2.03×10?4MPa和15.33%,与苎麻纤维性能相似,可满足可纺性要求.并有一定的保暖性和优良的抑菌效果.
為瞭提取一種新型植物纖維-烏拉草纖維併研究其性能,採用超聲波-堿氧-浴法從烏拉草秸稈中提取烏拉草纖維,用多指標正交試驗方法對超聲波時間,堿煮時間,堿用量和雙氧水用量進行優化設計,併通過對直徑,斷裂彊度,迴潮率3箇指標的綜閤分析評價確定最佳提取工藝,對處理後的烏拉草纖維進行基本性能測試及保暖、抗菌效果測試.結果錶明:最佳工藝參數為:超聲波時間為70 min;堿氧-浴時間為100 min;0.75 L溶液中堿質量濃度為8 g/L;雙氧水質量濃度為12 g/L.採用最優工藝所提取的烏拉草纖維平均直徑、長度、斷裂彊度及迴潮率分彆為47.19μm、152.59 mm、2.03×10?4MPa和15.33%,與苧痳纖維性能相似,可滿足可紡性要求.併有一定的保暖性和優良的抑菌效果.
위료제취일충신형식물섬유-오랍초섬유병연구기성능,채용초성파-감양-욕법종오랍초갈간중제취오랍초섬유,용다지표정교시험방법대초성파시간,감자시간,감용량화쌍양수용량진행우화설계,병통과대직경,단렬강도,회조솔3개지표적종합분석평개학정최가제취공예,대처리후적오랍초섬유진행기본성능측시급보난、항균효과측시.결과표명:최가공예삼수위:초성파시간위70 min;감양-욕시간위100 min;0.75 L용액중감질량농도위8 g/L;쌍양수질량농도위12 g/L.채용최우공예소제취적오랍초섬유평균직경、장도、단렬강도급회조솔분별위47.19μm、152.59 mm、2.03×10?4MPa화15.33%,여저마섬유성능상사,가만족가방성요구.병유일정적보난성화우량적억균효과.
In order to prepare a new kind of natural fibers and analysis its properties, the curaua fiber was extracted by the method of ultrasound-alkali-H2O2 one-bath technology. The four parameters of ultrasonic time, alkali treatment time, the concentrations of NaOH and H2O2 were optimized by multiple indicator orthogonal experimental method based on the evaluation factors of fibers diameter, breaking strength and moisture regain. The basic physical properties, adiathermic property together with the antibacterial property of curaua fibers were evaluated. Further more, the mechanism of adiathermic property and the antibacterial composition were explored. The results show that the optimal parameters were ultrasonic time of 70 min, alkali-oxygen one bath time of 100 min, alkali weight concentration of 8 g/L, hydrogen peroxide weight concentration of 12 g/L in the solution of 0.75 L. The extracted curaua fibers are 47.19 μm in diameter, 152.59 mm in length, 2.03×10?4 MPa in tensile strength and 15.33% in moisture regain, which are comparable with ramie fibers. The curaua/cotton(70/30) net with the CLO value of 1.316 and the thermal resistance of 0.204 m2·K/W, has certain warmth retention property, which is slightly lower than wool fibers net. In vitro antibacterial test,we found that curaua fiber has excellent antibacterial effect to colibacillus and staphylocccus aureus. In addition, the SEM pictures show that there are lumens in the cross section of the fibers. The filter liquor of curaua fiber has flavonoids of antimicrobial substances, which was tested by the ultraviolet spectroscopy.