CuCr0.91Mg0.09O2 thin film%rectifying characteristic%series resistance%synthesis%electrical properties
利用射频磁控溅射制备p-CuCr0.91Mg0.09O2/n-Si异质结.XRD结果表明所制备的纯相CuCr0.91Mg0.09O2薄膜具有(012)取向生长特点,正的霍尔系数确定薄膜的 p 型特性;电流—电压特性测试结果显示 p-CuCr0.91- Mg0.09O2/n-Si异质结具有明显的整流特性,结的开启电压约为1.0 V,在?5.0~5.0 V的电压范围内正向电压与反向方向电压比约为8.2.基于p-n+单边突变结理论,对p-CuCr0.91Mg0.09O2/n-Si异质结的电流曲线进行模拟,模拟结果表明界面状态和串联电阻是影响结整流特性性质的重要因素.
利用射頻磁控濺射製備p-CuCr0.91Mg0.09O2/n-Si異質結.XRD結果錶明所製備的純相CuCr0.91Mg0.09O2薄膜具有(012)取嚮生長特點,正的霍爾繫數確定薄膜的 p 型特性;電流—電壓特性測試結果顯示 p-CuCr0.91- Mg0.09O2/n-Si異質結具有明顯的整流特性,結的開啟電壓約為1.0 V,在?5.0~5.0 V的電壓範圍內正嚮電壓與反嚮方嚮電壓比約為8.2.基于p-n+單邊突變結理論,對p-CuCr0.91Mg0.09O2/n-Si異質結的電流麯線進行模擬,模擬結果錶明界麵狀態和串聯電阻是影響結整流特性性質的重要因素.
이용사빈자공천사제비p-CuCr0.91Mg0.09O2/n-Si이질결.XRD결과표명소제비적순상CuCr0.91Mg0.09O2박막구유(012)취향생장특점,정적곽이계수학정박막적 p 형특성;전류—전압특성측시결과현시 p-CuCr0.91- Mg0.09O2/n-Si이질결구유명현적정류특성,결적개계전압약위1.0 V,재?5.0~5.0 V적전압범위내정향전압여반향방향전압비약위8.2.기우p-n+단변돌변결이론,대p-CuCr0.91Mg0.09O2/n-Si이질결적전류곡선진행모의,모의결과표명계면상태화천련전조시영향결정류특성성질적중요인소.
@@@@The p-CuCr0.91Mg0.09O2/n-Si p-n heterogenous junction was synthesized by the radio-frequency magnetron sputtering. The XRD results show that the p-CuCr0.91Mg0.09O2 thin film tends to be oriented on the (012) plane, the positive Hall coefficient confirms p-type nature of the film. The current—voltage characteristic test results show that p-Cu- Cr0.91Mg0.09O2/n-Si heterogenous junction is of obvious rectifying, the ratio of forward current to the reverse current is about 8.2 within the applied voltage range of –5.0 ? 5.0 V and the turn-on voltage is about 1.0 V. The p-CuCr0.91Mg0.09O2/n-Si p-n heterogenous junction can be fitted by the theory of p-n+ one-sided step junction, the simulated results indicate that the effects of the interface state and series resistance are important factors for the rectifying property of the junction.