通过热力学计算研究稀土Ce夹杂物在高铁扣件弹簧钢中生成的热力学条件,并分析加入稀土Ce对Al2O3夹杂的变质作用及条件.由稀土Ce硫化物、氧化物和氧硫化物的标准吉布斯生成自由能构建了稀土Ce夹杂物的空间析出图,并将其应用在预测高铁扣件弹簧钢中加入稀土Ce后夹杂物的生成顺序,并确定其存在形式及热力学转换条件.计算结果表明:钢液中加入稀土最容易生成的是CeAlO3夹杂,其次是Ce2O2S;在本计算所用钢种的氧活度和硫活度分别为0.000639和0.005845的条件下,钢液中首先会析出Ce2O2S;当钢液中Al含量为0.013%时,稀土变质Al2O3夹杂的理论加入量为0.0019%.
通過熱力學計算研究稀土Ce夾雜物在高鐵釦件彈簧鋼中生成的熱力學條件,併分析加入稀土Ce對Al2O3夾雜的變質作用及條件.由稀土Ce硫化物、氧化物和氧硫化物的標準吉佈斯生成自由能構建瞭稀土Ce夾雜物的空間析齣圖,併將其應用在預測高鐵釦件彈簧鋼中加入稀土Ce後夾雜物的生成順序,併確定其存在形式及熱力學轉換條件.計算結果錶明:鋼液中加入稀土最容易生成的是CeAlO3夾雜,其次是Ce2O2S;在本計算所用鋼種的氧活度和硫活度分彆為0.000639和0.005845的條件下,鋼液中首先會析齣Ce2O2S;噹鋼液中Al含量為0.013%時,稀土變質Al2O3夾雜的理論加入量為0.0019%.
통과열역학계산연구희토Ce협잡물재고철구건탄황강중생성적열역학조건,병분석가입희토Ce대Al2O3협잡적변질작용급조건.유희토Ce류화물、양화물화양류화물적표준길포사생성자유능구건료희토Ce협잡물적공간석출도,병장기응용재예측고철구건탄황강중가입희토Ce후협잡물적생성순서,병학정기존재형식급열역학전환조건.계산결과표명:강액중가입희토최용역생성적시CeAlO3협잡,기차시Ce2O2S;재본계산소용강충적양활도화류활도분별위0.000639화0.005845적조건하,강액중수선회석출Ce2O2S;당강액중Al함량위0.013%시,희토변질Al2O3협잡적이론가입량위0.0019%.
@@@@Thermodynamic condition of rare earth cerium inclusion formed in spring steel used in fastener of high-speed railway was studied by the thermodynamic calculation. In addition, the effect and condition of rare earth cerium on modifying Al2O3 inclusion were analyzed. Through the standard Gibbs free energies of formation of the sulfides, oxides and oxysulfides of cerium, the precipitation diagram in space was built. And it was applied to predict the sequence of rare earth inclusion formed the spring steel. Finally, the ultimate state of rare earth inclusions and their thermodynamic transformation condition were determined. The computation results show that the most easily formed inclusion is CeAlO3 when rare earth element Ce is added to the molten steel, with Ce2O2S following. In this work, when the activities of oxygen and sulfur in the steel are 0.000 639 and 0.005 845, respectively, the first precipitated inclusion is Ce2O2S. Moreover, when the aluminum content in the steel is 0.013%, the theoretic amount of added rare earth Ce is 0.0019%, which can realize Al2O3 deformation.