本文在采用自制阳离子改性剂对CVC织物改性的基础上,探索研究了新型涂料轧染工艺.通过对涂料轧染中粘合剂、交联剂用量以及焙烘温度和时间的优化,获得了较高的K/S值和耐皂洗、耐摩色牢度.优化后的工艺条件为涂料6 g/L,粘合剂DH-103用量15 g/L,Araldite PT810交联剂10 g/L,180℃焙烘3 min.
본문재채용자제양리자개성제대CVC직물개성적기출상,탐색연구료신형도료알염공예.통과대도료알염중점합제、교련제용량이급배홍온도화시간적우화,획득료교고적K/S치화내조세、내마색뇌도.우화후적공예조건위도료6 g/L,점합제DH-103용량15 g/L,Araldite PT810교련제10 g/L,180℃배홍3 min.
A new pigment padding process was explored on the basis of modified CVC fabric treated by self-made cationic modification agent. The dosages of adhesive and crosslinking agent, the curing temperature and time were optimized to obtain higher K/S value and color fastness to washing and rubbing. The results showed that the optimum condition was as follows:pigment 6 g/L, binder DH-103 15 g/L, Araldite PT810 crosslinking agent 10 g/L, curing at 180℃for 3 min.