CAJ | 학술논문

在3.5% NaCl(质量分数)溶液中测定铸态和经固溶处理的Mg-6Al-5Pb-1.5In镁合金阳极的腐蚀电化学性能,采用金相(OM)、扫描电镜(SEM)和能谱分析(EDS)分别研究其显微组织、截面腐蚀形貌及相组成.结果表明:固溶后β-Mg17Al12相基本溶入α-Mg基体,降低微电偶腐蚀中阴极与阳极的面积比,增大阳极自腐蚀速率;Mg2Pb相的自腐蚀电位比镁基体正,固溶后Pb以Mg2Pb相析出,阳极表面腐蚀后晶粒中央的Mg2Pb相并没有被腐蚀.Al含量是决定镁阳极中各相腐蚀速率的关键,相表面形成的保护膜中Al含量越高,对基体保护性能越好.
재3.5% NaCl(질량분수)용액중측정주태화경고용처리적Mg-6Al-5Pb-1.5In미합금양겁적부식전화학성능,채용금상(OM)、소묘전경(SEM)화능보분석(EDS)분별연구기현미조직、절면부식형모급상조성.결과표명:고용후β-Mg17Al12상기본용입α-Mg기체,강저미전우부식중음겁여양겁적면적비,증대양겁자부식속솔;Mg2Pb상적자부식전위비미기체정,고용후Pb이Mg2Pb상석출,양겁표면부식후정립중앙적Mg2Pb상병몰유피부식.Al함량시결정미양겁중각상부식속솔적관건,상표면형성적보호막중Al함량월고,대기체보호성능월호.
@@@@The corrosion electrochemical properties of as-cast and solid-solution-treated Mg-6Al-5Pb-1.5In alloy anodes were examined in 3.5%NaCl (mass fraction) solution. The microstructures, cross-sectional corrosion morphologies and composition of phases in the anodes were studied by optical microscopy (OM), scanning electronic microscopy (SEM)and energy dispersive spectrometry (EDS), respectively. The experimental results show that, theβ-Mg17Al12 phase dissolves into the α-Mg matrix, the cathode-to-anode area ratio of the anodes decreases, and the self-corrosion rates increase after solution treatment. Pb segregates in the form of Mg2Pb and the electro-negativity of Mg2Pb is more positive than that of theα-Mg matrix, which results in the un-corroded Mg2Pb existing in the center of the corroded area at the surfaces of anodes. The aluminum content is a dominant factor of corrosion rate in magnesium anodes, and the higher the aluminum content of the protective film is, the better the protective properties to matrix is.