二氧化锆陶瓷%自粘接树脂水门汀%粘接强度%粘接耐久性%研磨%喷砂
二氧化鋯陶瓷%自粘接樹脂水門汀%粘接彊度%粘接耐久性%研磨%噴砂
이양화고도자%자점접수지수문정%점접강도%점접내구성%연마%분사
zirconia ceramic%self-adhesive resin cement%bond strength%bond durability%polishing%sand-blasting
目的比较不同自粘接树脂水门汀与二氧化锆陶瓷间的粘接强度和耐久能力.方法二氧化锆陶瓷片经烧结、研磨后,接受50μm Al2O3颗粒喷砂处理.使用激光共聚焦显微镜对研磨、喷砂处理的陶瓷表面粗糙度进行测量.研磨、喷砂处理的陶瓷片分别与5种自粘接树脂水门汀: Biscem(BC)、 G-Cem(GC)、 RelyX U100(RU)、Multilink Speed(MS)、 Maxcem(MC)进行粘接.每组粘接试件分为2个亚组分别接受0、10000次冷热循环后进行剪切粘接强度测量.使用单因素方差和独立样本t检验对数据进行分析.结果喷砂处理明显增加了陶瓷表面粗糙度指标Ra值(P<0.001).冷热循环降低了所有实验组的粘接强度(P<0.001),其中研磨处理陶瓷片与MS组的粘接强度明显高于与BC组、 GC组、 RU组和MC组(P<0.001),喷砂处理明显提高了BC组、 GC组、 RU组和MC组的粘接强度(P<0.001).结论不同自粘接树脂水门汀与二氧化锆陶瓷间的粘接耐久能力存在明显差异,其粘接耐久能力不完全受陶瓷表面喷砂处理的影响.
目的比較不同自粘接樹脂水門汀與二氧化鋯陶瓷間的粘接彊度和耐久能力.方法二氧化鋯陶瓷片經燒結、研磨後,接受50μm Al2O3顆粒噴砂處理.使用激光共聚焦顯微鏡對研磨、噴砂處理的陶瓷錶麵粗糙度進行測量.研磨、噴砂處理的陶瓷片分彆與5種自粘接樹脂水門汀: Biscem(BC)、 G-Cem(GC)、 RelyX U100(RU)、Multilink Speed(MS)、 Maxcem(MC)進行粘接.每組粘接試件分為2箇亞組分彆接受0、10000次冷熱循環後進行剪切粘接彊度測量.使用單因素方差和獨立樣本t檢驗對數據進行分析.結果噴砂處理明顯增加瞭陶瓷錶麵粗糙度指標Ra值(P<0.001).冷熱循環降低瞭所有實驗組的粘接彊度(P<0.001),其中研磨處理陶瓷片與MS組的粘接彊度明顯高于與BC組、 GC組、 RU組和MC組(P<0.001),噴砂處理明顯提高瞭BC組、 GC組、 RU組和MC組的粘接彊度(P<0.001).結論不同自粘接樹脂水門汀與二氧化鋯陶瓷間的粘接耐久能力存在明顯差異,其粘接耐久能力不完全受陶瓷錶麵噴砂處理的影響.
목적비교불동자점접수지수문정여이양화고도자간적점접강도화내구능력.방법이양화고도자편경소결、연마후,접수50μm Al2O3과립분사처리.사용격광공취초현미경대연마、분사처리적도자표면조조도진행측량.연마、분사처리적도자편분별여5충자점접수지수문정: Biscem(BC)、 G-Cem(GC)、 RelyX U100(RU)、Multilink Speed(MS)、 Maxcem(MC)진행점접.매조점접시건분위2개아조분별접수0、10000차랭열순배후진행전절점접강도측량.사용단인소방차화독립양본t검험대수거진행분석.결과분사처리명현증가료도자표면조조도지표Ra치(P<0.001).랭열순배강저료소유실험조적점접강도(P<0.001),기중연마처리도자편여MS조적점접강도명현고우여BC조、 GC조、 RU조화MC조(P<0.001),분사처리명현제고료BC조、 GC조、 RU조화MC조적점접강도(P<0.001).결론불동자점접수지수문정여이양화고도자간적점접내구능력존재명현차이,기점접내구능력불완전수도자표면분사처리적영향.
@@@@Objective To compare the bond durability of five self-adhesive resin cements to polished and sand-blasted zirconia ceramic. Methods Zirconia ceramic samples were sintered and polished. Half of polished ceramic samples were sandblasted with 50μm alumina particles. The roughness of polished and sandblasted zirconia ceramic surface was measured by 3D-laser scanning microscope. The polished and sandblasted ceramic samples were bonded to composite cylinders with either Biscem(BC), G-Cem(GC), RelyX U100(RU), Multilink Speed(MS) or Maxcem (MC). The samples divided into two subgroups to receive respectively shear test after 0 and 10 000 time thermal cy-cles. The data were analyzed by one-way ANOVA test and independent sample t test. Results Air abrasion signifi-cantly increased Ra of zirconia ceramic surface(P<0.001). Thermocycling decreased significantly the bond strengths of all test groups(P<0.001), in which polished specimens bonded with MS had significantly higher bond strength than those bonded with either BC, GC, RU, or MC(P<0.001), and air abrasion significantly increased the bond strength of BC, GC, RU and MC, whereas the bond strength of MS was not significantly affected by air abrasion. Conclusion The bond durability of different self-adhesive resin cements to zirconia ceramic has significant differences, and their bond durability was not completely influenced by air abrasion of ceramic surface.