在外加磁场作用下,制备出Ni纳米线,再以Ni纳米线为载体,利用 Ni 置换溶液中的 Cu2＋制备出Ni/Cu双金属纳米线,并进行扫描电镜(SEM)、透射电镜(TEM)、X 射线衍射(XRD)、能谱(EDS)等表征.结果显示样品线性较好、尺寸均匀,约为200 nm,组成为Ni单质和Cu单质,均为面心立方结构,其含量分别为62．34％与36．37％(质量分数).
재외가자장작용하,제비출Ni납미선,재이Ni납미선위재체,이용 Ni 치환용액중적 Cu2＋제비출Ni/Cu쌍금속납미선,병진행소묘전경(SEM)、투사전경(TEM)、X 사선연사(XRD)、능보(EDS)등표정.결과현시양품선성교호、척촌균균,약위200 nm,조성위Ni단질화Cu단질,균위면심립방결구,기함량분별위62．34％여36．37％(질량분수).
Under a magnetic field,nickel nanowires were synthesized by a template-free method,and Ni/Cu bi-metal nanowires were synthesized using as-prepared nickel nanowires as carriers.The products were character-ized by SEM,TEM,XRD,EDS.The results showed that the Ni/Cu bimetal nanowires had uniform size and morphology,about 200 nm,and were composed of Ni(face-centered cubic,fcc)and Cu(fcc),the content of Ni and Cu in the products were 62.34wt% and 36.37wt%,respectively.