研究了废弃含溴化阻燃剂的电子塑料在超临界异丙醇中的液化特性.研究结果表明塑料在超临界异丙醇中发生了解聚,产生油、气以及固体残渣,塑料中的溴化阻燃剂发生了脱溴降解.反应时间、固/液比、溶剂填充度对塑料解聚及阻燃剂脱溴降解影响较大,在最佳工艺条件(温度：400℃,反应时间：60min,固/液比：1/10,溶剂填充度：50%)下获得60%的产油率及95.3%的脱溴率.油以苯系物及酚类物质为主要组成物质,其热值为37.5MJ/kg.超临界异丙醇处理含溴化阻燃剂塑料主要包括溴化阻燃剂的萃取、脱溴降解和塑料高温解聚等过程.
연구료폐기함추화조연제적전자소료재초림계이병순중적액화특성.연구결과표명소료재초림계이병순중발생료해취,산생유、기이급고체잔사,소료중적추화조연제발생료탈추강해.반응시간、고/액비、용제전충도대소료해취급조연제탈추강해영향교대,재최가공예조건(온도：400℃,반응시간：60min,고/액비：1/10,용제전충도：50%)하획득60%적산유솔급95.3%적탈추솔.유이분계물급분류물질위주요조성물질,기열치위37.5MJ/kg.초림계이병순처리함추화조연제소료주요포괄추화조연제적췌취、탈추강해화소료고온해취등과정.
Liquefaction properties of waste electrical plastic containing brominated flame retardant (BFR) in supercritical isopropanol were investigated. Results indicated that the plastic was degraded to oil, gas and solid residue. Simultaneously, BFR was debrominated. The degradation efficiencies, oil yields, debromination efficiencies and oil composition were significantly influenced by reaction time, solid/solvent ratio and solvent filling ratio. Under the optimum conditions (temperature: 400℃, reaction time: 60min, solid/solvent ratio: 1/10, solvent filling ratio: 50%), the oil yield and debromination efficiency were 60%and 95.3%, respectively. The oil was composed of benzene substances and phenolic compounds without organobromine compounds. The calorific value of oil was 37.5MJ/kg. The mechanism of treatment of plastic containing BFR was proposed:BFR was firstly abstracted by supercritical fluid and then decomposed in the fluid;the plastic was also decomposed at higher temperature.