功能材料
功能材料
공능재료
JOURNAL OF FUNCTIONAL MATERIALS
2015年
2期
2066-2069,2075
,共5页
谢春晓%杨元政%钟守炎%李胜%邓世春
謝春曉%楊元政%鐘守炎%李勝%鄧世春
사춘효%양원정%종수염%리성%산세춘
非晶合金%热处理%晶化过程%磁性能
非晶閤金%熱處理%晶化過程%磁性能
비정합금%열처리%정화과정%자성능
amorphous alloys%heat treatment%crystallization processes%magnetic properties
采用单辊急冷法制备了一系列不同 Cr/Mo比的 FeCoMoCrZr 非晶薄带,并对该系非晶合金进行等温热处理.用 XRD和 VSM研究 Cr/Mo 比的变化对(Fe0.58 Co0.42)73 Mo17-x Crx Zr10系非晶合金晶化过程和磁性能的影响.结果表明,x 在9~17之间变化时,所制备的合金薄带为非晶结构;(Fe0.58 Co0.42)73 Mo5 Cr12 Zr10非晶合金的晶化过程为:Am →α-Fe(Co)+CrFe4+Fe23 Zr6+Cr2 Mo,(Fe0.58 Co0.42)73 Cr17 Zr10非晶合金的晶化过程为:Am →α-Fe(Co)+ Am′→α-Fe(Co)+ CrFe4+Fe3 Ni2+未知相;Cr/Mo 比例的增加降低了合金的热稳定性,促进了退火后α-Fe(Co)相的析出.两种合金的饱和磁化强度Ms随退火温度的变化趋势相同但幅度不同,在低于晶化峰值温度Tp退火,(Fe0.58 Co0.42)73 Mo5 Cr12 Zr10合金的Ms随退火温度的升高缓慢上升;而(Fe0.58 Co0.42)73 Cr17 Zr10合金的Ms随退火温度的升高快速大幅上升.
採用單輥急冷法製備瞭一繫列不同 Cr/Mo比的 FeCoMoCrZr 非晶薄帶,併對該繫非晶閤金進行等溫熱處理.用 XRD和 VSM研究 Cr/Mo 比的變化對(Fe0.58 Co0.42)73 Mo17-x Crx Zr10繫非晶閤金晶化過程和磁性能的影響.結果錶明,x 在9~17之間變化時,所製備的閤金薄帶為非晶結構;(Fe0.58 Co0.42)73 Mo5 Cr12 Zr10非晶閤金的晶化過程為:Am →α-Fe(Co)+CrFe4+Fe23 Zr6+Cr2 Mo,(Fe0.58 Co0.42)73 Cr17 Zr10非晶閤金的晶化過程為:Am →α-Fe(Co)+ Am′→α-Fe(Co)+ CrFe4+Fe3 Ni2+未知相;Cr/Mo 比例的增加降低瞭閤金的熱穩定性,促進瞭退火後α-Fe(Co)相的析齣.兩種閤金的飽和磁化彊度Ms隨退火溫度的變化趨勢相同但幅度不同,在低于晶化峰值溫度Tp退火,(Fe0.58 Co0.42)73 Mo5 Cr12 Zr10閤金的Ms隨退火溫度的升高緩慢上升;而(Fe0.58 Co0.42)73 Cr17 Zr10閤金的Ms隨退火溫度的升高快速大幅上升.
채용단곤급랭법제비료일계렬불동 Cr/Mo비적 FeCoMoCrZr 비정박대,병대해계비정합금진행등온열처리.용 XRD화 VSM연구 Cr/Mo 비적변화대(Fe0.58 Co0.42)73 Mo17-x Crx Zr10계비정합금정화과정화자성능적영향.결과표명,x 재9~17지간변화시,소제비적합금박대위비정결구;(Fe0.58 Co0.42)73 Mo5 Cr12 Zr10비정합금적정화과정위:Am →α-Fe(Co)+CrFe4+Fe23 Zr6+Cr2 Mo,(Fe0.58 Co0.42)73 Cr17 Zr10비정합금적정화과정위:Am →α-Fe(Co)+ Am′→α-Fe(Co)+ CrFe4+Fe3 Ni2+미지상;Cr/Mo 비례적증가강저료합금적열은정성,촉진료퇴화후α-Fe(Co)상적석출.량충합금적포화자화강도Ms수퇴화온도적변화추세상동단폭도불동,재저우정화봉치온도Tp퇴화,(Fe0.58 Co0.42)73 Mo5 Cr12 Zr10합금적Ms수퇴화온도적승고완만상승;이(Fe0.58 Co0.42)73 Cr17 Zr10합금적Ms수퇴화온도적승고쾌속대폭상승.
Amorphous ribbons of the FeCoMoCrZr alloy with different Cr/Mo ratios were prepared by melt-spun method and annealed at different temperatures.X-ray diffraction and vibrating sample magnetometer were adopted to study the effect of Cr/Mo ratios on the crystallization processes and magnetic properties of (Fe0.5 8 Co0.42)73Mo17-xCrxZr10 amorphous ribbons.The results show that when x ranges from 9 to 17,the ribbons are in an amorphous state.The crystallization process of (Fe0.58 Co0.42 )73 Mo5 Cr12 Zr10 is Am →α-Fe(Co)+ CrFe4+Fe23 Zr6+Cr2 Mo,but the crystallization process of (Fe0.58 Co0.42 )73 Cr17 Zr10 is Am →α-Fe(Co)+ Am′→α-Fe (Co)+ CrFe4+ Fe3 Ni2+ unidentified phase;Increasing Cr/Mo ratios decrease the thermal stability of the al-loys and increase the precipitation ofα-Fe(Co)after annealing.The changing of magnetic properties of the two alloys are different with increasing annealing temperature.Annealed below Tp ,the value of saturation magneti-zation Ms of (Fe0.58 Co0.42 )73 Mo5 Cr12 Zr10 alloy increases slowly with increasing the annealing temperature,but the Ms of (Fe0.58 Co0.42 )73 Cr17 Zr10 alloy increases quickly with increasing the annealing temperature.