建筑科学与工程学报
建築科學與工程學報
건축과학여공정학보
JOURNAL OF ARCHITECTURE AND CIVIL ENGINEERING
2014年
4期
1-6
,共6页
吴方伯%李钧%邓利斌%岳建武%周绪红
吳方伯%李鈞%鄧利斌%嶽建武%週緒紅
오방백%리균%산리빈%악건무%주서홍
钢筋混凝土%密肋薄腹梁%抗剪性能%开裂荷载%极限荷载%破坏特征
鋼觔混凝土%密肋薄腹樑%抗剪性能%開裂荷載%極限荷載%破壞特徵
강근혼응토%밀륵박복량%항전성능%개렬하재%겁한하재%파배특정
reinforced concrete%multi-ribbed thin web beam%shear behavior%cracking load%ulti-mate load%failure characteristic
进行了4根大尺寸钢筋混凝土密肋薄腹梁在集中荷载作用下的抗剪性能试验,对其主要受力过程、开裂荷载、破坏特征及抗剪承载力进行了对比分析。结果表明:试验密肋薄腹梁的主要受力过程及破坏特征与普通有腹筋梁相似;有预制底板的试件开裂荷载和极限荷载比无预制底板的试件大,预制底板的存在还提高了试件的抗弯刚度和整体工作性能;通过分析4根试件抗剪承载力试验结果及破坏特征可知,受剪箍筋能否得到充分利用,在很大程度上取决于主斜裂缝的位置及倾角等因素;通过承载力的试验值与各主要规范计算值进行对比可知,由于各规范考虑因素及侧重程度不同,抗剪承载力计算值相差较大,中国规范和德国规范计算值与试验值比值最小,美国规范和英国规范比值最大。
進行瞭4根大呎吋鋼觔混凝土密肋薄腹樑在集中荷載作用下的抗剪性能試驗,對其主要受力過程、開裂荷載、破壞特徵及抗剪承載力進行瞭對比分析。結果錶明:試驗密肋薄腹樑的主要受力過程及破壞特徵與普通有腹觔樑相似;有預製底闆的試件開裂荷載和極限荷載比無預製底闆的試件大,預製底闆的存在還提高瞭試件的抗彎剛度和整體工作性能;通過分析4根試件抗剪承載力試驗結果及破壞特徵可知,受剪箍觔能否得到充分利用,在很大程度上取決于主斜裂縫的位置及傾角等因素;通過承載力的試驗值與各主要規範計算值進行對比可知,由于各規範攷慮因素及側重程度不同,抗剪承載力計算值相差較大,中國規範和德國規範計算值與試驗值比值最小,美國規範和英國規範比值最大。
진행료4근대척촌강근혼응토밀륵박복량재집중하재작용하적항전성능시험,대기주요수력과정、개렬하재、파배특정급항전승재력진행료대비분석。결과표명:시험밀륵박복량적주요수력과정급파배특정여보통유복근량상사;유예제저판적시건개렬하재화겁한하재비무예제저판적시건대,예제저판적존재환제고료시건적항만강도화정체공작성능;통과분석4근시건항전승재력시험결과급파배특정가지,수전고근능부득도충분이용,재흔대정도상취결우주사렬봉적위치급경각등인소;통과승재력적시험치여각주요규범계산치진행대비가지,유우각규범고필인소급측중정도불동,항전승재력계산치상차교대,중국규범화덕국규범계산치여시험치비치최소,미국규범화영국규범비치최대。
T he experiment on the shear behavior of four large‐size reinforced concrete multi‐ribbed thin web beams under concentrated loading was carried out , the force processes of bearing capacity ,cracking load ,failure characteristic and shear capacity were comparatively analyzed . T he results indicate that the force process of bearing capacity and failure characteristic of the multi‐ribbed thin web beams is similar to that of normal beams with web reinforcement .The cracking load and ultimate load of the specimen with precast floor are larger than specimen without precast floor .The flexural stiffness and overall operating performance of the specimens are improved by precast floor . Through the analysis of shear capacity of four specimens'experiment values and failure characteristic ,it is obtained that w hether the shear stirrup be fully utilized ,depends on the location and the angle of diagonal crack to a great extent .The comparing of ultimate shear capacities of experiment values and the calculated values according to various code provisions indicate that due to the main factors of code in some countries on different levels , the calculated values of shear capacity are not the same .The measured‐to‐calculated ratio of shear capacity is minimum by Chinese code and Germany code ,and the ratio is maximum by American code and United Kingdom code .