王岚%胡江三%陈刚%弓宁宁
王嵐%鬍江三%陳剛%弓寧寧
왕람%호강삼%진강%궁저저
VIC-3 D技术%界面%位移场%应变场%裂缝
VIC-3 D技術%界麵%位移場%應變場%裂縫
VIC-3 D기술%계면%위이장%응변장%렬봉
video image correlate-3D%interface%displacement field%strain field%crack
为研究沥青混合料开裂及裂缝发展规律,通过SBS 改性沥青混合料半圆试件三点弯曲实验,基于数字图像相关技术,利用 VIC-3D(video image corre-late,3D)采集系统对试件从加载到破坏全过程进行图像采集,并利用 VIC-3 D 软件计算得到试件在受弯拉过程中三维位移场、应变场的变化及变化速率,分析并得出裂缝出现及发展规律;利用扫描电子显微镜对开裂试件断口进行观察,结合位移场、应变场及其变化速率揭示了试件开裂及裂缝发展的机理。结果表明,利用水平方向应变随时间变化规律可探究裂缝的发展轨迹;沥青混合料的开裂和裂缝发展沿沥青砂浆与粗集料的界面区发生,且趋向于表面情况相对差的集料的界面区;裂缝发展速率与界面区的厚度有关,可根据界面区厚度的代表值预测裂缝发展速率。
為研究瀝青混閤料開裂及裂縫髮展規律,通過SBS 改性瀝青混閤料半圓試件三點彎麯實驗,基于數字圖像相關技術,利用 VIC-3D(video image corre-late,3D)採集繫統對試件從加載到破壞全過程進行圖像採集,併利用 VIC-3 D 軟件計算得到試件在受彎拉過程中三維位移場、應變場的變化及變化速率,分析併得齣裂縫齣現及髮展規律;利用掃描電子顯微鏡對開裂試件斷口進行觀察,結閤位移場、應變場及其變化速率揭示瞭試件開裂及裂縫髮展的機理。結果錶明,利用水平方嚮應變隨時間變化規律可探究裂縫的髮展軌跡;瀝青混閤料的開裂和裂縫髮展沿瀝青砂漿與粗集料的界麵區髮生,且趨嚮于錶麵情況相對差的集料的界麵區;裂縫髮展速率與界麵區的厚度有關,可根據界麵區厚度的代錶值預測裂縫髮展速率。
위연구력청혼합료개렬급렬봉발전규률,통과SBS 개성력청혼합료반원시건삼점만곡실험,기우수자도상상관기술,이용 VIC-3D(video image corre-late,3D)채집계통대시건종가재도파배전과정진행도상채집,병이용 VIC-3 D 연건계산득도시건재수만랍과정중삼유위이장、응변장적변화급변화속솔,분석병득출렬봉출현급발전규률;이용소묘전자현미경대개렬시건단구진행관찰,결합위이장、응변장급기변화속솔게시료시건개렬급렬봉발전적궤리。결과표명,이용수평방향응변수시간변화규률가탐구렬봉적발전궤적;력청혼합료적개렬화렬봉발전연력청사장여조집료적계면구발생,차추향우표면정황상대차적집료적계면구;렬봉발전속솔여계면구적후도유관,가근거계면구후도적대표치예측렬봉발전속솔。
In order to study the cracking and the development of crack of asphalt mixture,three point bending of semicircular specimens of SBS asphalt mixture was conducted.Based on digital image correlate,VIC-3D (video image correlate,3D)acquisition system and the calculation software was used respectively during the whole damage process of specimens for image acquisition and calculation of displacement field,strain field and the changing rate of them,the cracking and the development of crack were obtained.Then the crack position of specimens was observed using scanning electron microscope and principle of cracking and the development of crack were explained with the help of the analysis of the displacement field and strain field.The results show that:using the horizontal strain variation law with time to explore the traj ectory of cracks is reasonable,the fracture of specimens and the development of fracture both occur along the interface of asphalt mortar and coarse aggregate area,and tend to the interface of aggregates which have poor interface.The development rate of fracture related to the thickness of the interface area,so it can be predicted according to a representative value of the thickness of interface layer.