zirconium%copper%rare earth cerium%the aluminum electrical round rod%microstructure%mechanical properties
通过微观分析及力学性能测试等方法,研究添加定量 Ce、Cu 的基础上,不同含量 Zr (0.06%~0.18%)对铝合金电工圆杆组织与性能的影响.结果表明,添加 Cu(1.9%)可提高铝电工圆杆的抗拉强度,但降低导电率;复合添加的 Ce(0.2%)后,各项性能指标都有所提升;Zr 加入铝电工圆杆中主要形成 Al3 Zr相,并且弥散分布在晶界上,加入0.12%Zr 的合金能够在电导率降低不多的前提下获得较好的力学和耐热性能;加入0.18%Zr 时,粗大 Al3 Zr 粒子和稀土化合物相相互交织在一起呈短柄或粗大粒状分布,附近α-Al基体被挤压成层片状,导致力学性能下降.研究结果有望成为改善和提高铝电工圆杆性能的理论依据和新思路.
通過微觀分析及力學性能測試等方法,研究添加定量 Ce、Cu 的基礎上,不同含量 Zr (0.06%~0.18%)對鋁閤金電工圓桿組織與性能的影響.結果錶明,添加 Cu(1.9%)可提高鋁電工圓桿的抗拉彊度,但降低導電率;複閤添加的 Ce(0.2%)後,各項性能指標都有所提升;Zr 加入鋁電工圓桿中主要形成 Al3 Zr相,併且瀰散分佈在晶界上,加入0.12%Zr 的閤金能夠在電導率降低不多的前提下穫得較好的力學和耐熱性能;加入0.18%Zr 時,粗大 Al3 Zr 粒子和稀土化閤物相相互交織在一起呈短柄或粗大粒狀分佈,附近α-Al基體被擠壓成層片狀,導緻力學性能下降.研究結果有望成為改善和提高鋁電工圓桿性能的理論依據和新思路.
통과미관분석급역학성능측시등방법,연구첨가정량 Ce、Cu 적기출상,불동함량 Zr (0.06%~0.18%)대려합금전공원간조직여성능적영향.결과표명,첨가 Cu(1.9%)가제고려전공원간적항랍강도,단강저도전솔;복합첨가적 Ce(0.2%)후,각항성능지표도유소제승;Zr 가입려전공원간중주요형성 Al3 Zr상,병차미산분포재정계상,가입0.12%Zr 적합금능구재전도솔강저불다적전제하획득교호적역학화내열성능;가입0.18%Zr 시,조대 Al3 Zr 입자화희토화합물상상호교직재일기정단병혹조대립상분포,부근α-Al기체피제압성층편상,도치역학성능하강.연구결과유망성위개선화제고려전공원간성능적이론의거화신사로.
The effects of addition of Ce,Cu and Zr(0.06%-0.18%)on microstructure and properties of the alumi-num elctrical round rod were investigated usin microstructure analysis,electrical performance and mechanical properties test.The results of study were showed as follows:the tensile strength of the alminum electrical round rod can be improved when the Cu content was 1 .9%,but decreased its conductivity;each performance index was fined remarkably when the Ce content was 0.2%;The Al3 Zr phase resulting from addition of Zr to the aluminum elctrical round rod was distributed at the grain boundary,the alloy of high mechanical and thermal properties can be got by adding 0.12% Zr,at the same time,the conductivity of aluminum will not be reduced significantly;The Al3 Zr phase and the RE-containing intermetallic compounds in the shape of short shank or coarse granule were j oined together,α-Al matrix is pressed into the shape of lamellar,which leading to the reduction of mechanical properties.The research for the improvement of the performance of the aluminum elctrical round rod provides a theoretical basis and new ideas.