JOURNAL OF GUANGDONG UNIVERSITY OF TECHNOLOGY
2015年
1期
20-23
,共4页
蓝立财%赵韦人%钟剑明%王建青%余发波
藍立財%趙韋人%鐘劍明%王建青%餘髮波
람립재%조위인%종검명%왕건청%여발파
Sr2 CaMoO6%掺杂%发射率%红外辐射材料
Sr2 CaMoO6%摻雜%髮射率%紅外輻射材料
Sr2 CaMoO6%참잡%발사솔%홍외복사재료
Sr2 CaMoO6%doped%emissivity%infrared radiation materials
采用高温固相反应法,在1100℃下制备了Sr2 CaMoO6红外辐射材料,通过掺杂不同含量的Eu2+离子合成样品.利用X射线衍射( XRD)、红外光谱( IR)、拉曼光谱和红外辐射测试等方法测试了样品的结构与红外辐射性能,研究了体系中不同含量的Eu2+离子对样品红外发射率的性能影响.结果表明:随着Eu2+离子浓度的增加,样品的XRD、红外光谱、拉曼光谱和红外发射率均发生变化,且Eu2+离子在双钙钛矿结构中是以取代Sr2+格位而存在于晶格中的.当体系中Eu2+含量为5%时,样品红外发射率达到最大值,此时,3~5μm,8~14μm和1~22μm波段的平均发射率分别为0.886,0.936和0.915.
採用高溫固相反應法,在1100℃下製備瞭Sr2 CaMoO6紅外輻射材料,通過摻雜不同含量的Eu2+離子閤成樣品.利用X射線衍射( XRD)、紅外光譜( IR)、拉曼光譜和紅外輻射測試等方法測試瞭樣品的結構與紅外輻射性能,研究瞭體繫中不同含量的Eu2+離子對樣品紅外髮射率的性能影響.結果錶明:隨著Eu2+離子濃度的增加,樣品的XRD、紅外光譜、拉曼光譜和紅外髮射率均髮生變化,且Eu2+離子在雙鈣鈦礦結構中是以取代Sr2+格位而存在于晶格中的.噹體繫中Eu2+含量為5%時,樣品紅外髮射率達到最大值,此時,3~5μm,8~14μm和1~22μm波段的平均髮射率分彆為0.886,0.936和0.915.
채용고온고상반응법,재1100℃하제비료Sr2 CaMoO6홍외복사재료,통과참잡불동함량적Eu2+리자합성양품.이용X사선연사( XRD)、홍외광보( IR)、랍만광보화홍외복사측시등방법측시료양품적결구여홍외복사성능,연구료체계중불동함량적Eu2+리자대양품홍외발사솔적성능영향.결과표명:수착Eu2+리자농도적증가,양품적XRD、홍외광보、랍만광보화홍외발사솔균발생변화,차Eu2+리자재쌍개태광결구중시이취대Sr2+격위이존재우정격중적.당체계중Eu2+함량위5%시,양품홍외발사솔체도최대치,차시,3~5μm,8~14μm화1~22μm파단적평균발사솔분별위0.886,0.936화0.915.
The Eu2 +doped Sr2 CaMoO6 powders with high emissivity were fabricated by the traditional sol-id state reaction at the temperature of 1 100℃.The X-ray powder diffraction ( XRD) , infrared transmit-tance spectra ( IR) , Raman spectra and Infrared emission properties were examined to study the structure and the infrared emission properties of the samples.Also the effects of the different amount of Eu2+on the infrared emissivity were investigated.It was found that the XRD patterns, infrared transmittance spec-tra, Raman spectra and infrared emissivity would change according to the increase of the amount of Eu2+, and the Eu2+ions replace the Sr2+site in the structure.When the content of Eu2+is about 5%, the powders reach the highest emissivity with 0.886 at the range of 3~5μm , 0.936 at the range of 8~14 μm and 0.915 at 1~22 μm.