纳米 TiO2%改性%硅烷偶联剂%PVC 复合材料
納米 TiO2%改性%硅烷偶聯劑%PVC 複閤材料
납미 TiO2%개성%규완우련제%PVC 복합재료
nano TiO2%modification%silane coupling agent%PVC composite
利用硅烷偶联剂 KH–570对纳米 TiO2进行改性,探讨了改性工艺,通过正交试验得出改性的最佳工艺条件:分散液 pH=7.5,偶联剂加入量为7 mL,超声时间40 min,沉降实验和粒度分析结果表明,改性纳米 TiO2表面亲油性能显著提高,粒子间的团聚也得到改善。将改性及未改性纳米 TiO2加入 PVC 基体中,制得 PVC/纳米 TiO2复合材料,并对其进行紫外屏蔽性能测试和拉力测试。结果表明,添加改性纳米 TiO2的 PVC 复合材料紫外屏蔽性能和力学性能均显著高于添加未改性纳米 TiO2的材料,且当改性纳米 TiO2质量分数为3%时,PVC/改性纳米 TiO2材料的紫外屏蔽性能和力学性能最佳。
利用硅烷偶聯劑 KH–570對納米 TiO2進行改性,探討瞭改性工藝,通過正交試驗得齣改性的最佳工藝條件:分散液 pH=7.5,偶聯劑加入量為7 mL,超聲時間40 min,沉降實驗和粒度分析結果錶明,改性納米 TiO2錶麵親油性能顯著提高,粒子間的糰聚也得到改善。將改性及未改性納米 TiO2加入 PVC 基體中,製得 PVC/納米 TiO2複閤材料,併對其進行紫外屏蔽性能測試和拉力測試。結果錶明,添加改性納米 TiO2的 PVC 複閤材料紫外屏蔽性能和力學性能均顯著高于添加未改性納米 TiO2的材料,且噹改性納米 TiO2質量分數為3%時,PVC/改性納米 TiO2材料的紫外屏蔽性能和力學性能最佳。
이용규완우련제 KH–570대납미 TiO2진행개성,탐토료개성공예,통과정교시험득출개성적최가공예조건:분산액 pH=7.5,우련제가입량위7 mL,초성시간40 min,침강실험화립도분석결과표명,개성납미 TiO2표면친유성능현저제고,입자간적단취야득도개선。장개성급미개성납미 TiO2가입 PVC 기체중,제득 PVC/납미 TiO2복합재료,병대기진행자외병폐성능측시화랍력측시。결과표명,첨가개성납미 TiO2적 PVC 복합재료자외병폐성능화역학성능균현저고우첨가미개성납미 TiO2적재료,차당개성납미 TiO2질량분수위3%시,PVC/개성납미 TiO2재료적자외병폐성능화역학성능최가。
The silane coupling agent KH–570 modification process of nanometer TiO2 was discussed. The optimum technological conditions for modification obtained by orthogonal experiment is :pH value of dispersion=7.5,the volume of coupling agent for 7 mL,ultrasonic time 40 min. Sedimentation experiment and granularity analysis results show that the nanometer TiO2 oil-wet performance and agglomeration of particles are significantly improved under the condition of the modification. Modified and unmodified nanometer TiO2 were put into PVC matrix to make PVC/nano TiO2 composite and the ultraviolet shielding performance tests and tensile tests were carried out. The results show that the material UV shielding performance and mechanical properties of adding modified nanometer TiO2 composites are significantly higher than that of adding unmodified nano TiO2. When the adding quantity of modified TiO2 particle is 3%,the UV shielding and mechanical properties of PVC/nano TiO2 composite are optimum.