球磨%分散染料%微纳米级%分散剂%球磨介质
毬磨%分散染料%微納米級%分散劑%毬磨介質
구마%분산염료%미납미급%분산제%구마개질
bal mil ing%disperse dyes%micro- nano- size%dispersant%mil ing medium
采用氧化锆珠作为球磨介质,以木质素磺酸钠和萘磺酸钠甲醛缩合物为分散剂,讨论了球磨处理C.I. Disperse Red 60染料制备微纳米染料分散液的工艺参数对染料粒径和分散稳定性的影响.结果表明,不同直径氧化锆混合的球磨介质优于单一直径氧化锆,木质素磺酸钠与萘磺酸钠混合分散剂优于单一分散剂.当分散液中染料用量为20%,m(染料)∶m(分散剂)=1∶1,复合分散剂m(木质素磺酸钠CBOS-4)∶m(萘磺酸钠MF)=2∶1,多元醇添加剂用量为10%(对染液总质量),采用m(Φ=2 mm)∶m(Φ=1 mm)∶m(Φ=0.5 mm)=17.5∶65∶17.5混合氧化锆球珠作为介质,m(染料)∶m(介质)=1∶20,球磨48 h,得到了稳定的染料分散液,颗粒平均粒径D50为132 nm.
採用氧化鋯珠作為毬磨介質,以木質素磺痠鈉和萘磺痠鈉甲醛縮閤物為分散劑,討論瞭毬磨處理C.I. Disperse Red 60染料製備微納米染料分散液的工藝參數對染料粒徑和分散穩定性的影響.結果錶明,不同直徑氧化鋯混閤的毬磨介質優于單一直徑氧化鋯,木質素磺痠鈉與萘磺痠鈉混閤分散劑優于單一分散劑.噹分散液中染料用量為20%,m(染料)∶m(分散劑)=1∶1,複閤分散劑m(木質素磺痠鈉CBOS-4)∶m(萘磺痠鈉MF)=2∶1,多元醇添加劑用量為10%(對染液總質量),採用m(Φ=2 mm)∶m(Φ=1 mm)∶m(Φ=0.5 mm)=17.5∶65∶17.5混閤氧化鋯毬珠作為介質,m(染料)∶m(介質)=1∶20,毬磨48 h,得到瞭穩定的染料分散液,顆粒平均粒徑D50為132 nm.
채용양화고주작위구마개질,이목질소광산납화내광산납갑철축합물위분산제,토론료구마처리C.I. Disperse Red 60염료제비미납미염료분산액적공예삼수대염료립경화분산은정성적영향.결과표명,불동직경양화고혼합적구마개질우우단일직경양화고,목질소광산납여내광산납혼합분산제우우단일분산제.당분산액중염료용량위20%,m(염료)∶m(분산제)=1∶1,복합분산제m(목질소광산납CBOS-4)∶m(내광산납MF)=2∶1,다원순첨가제용량위10%(대염액총질량),채용m(Φ=2 mm)∶m(Φ=1 mm)∶m(Φ=0.5 mm)=17.5∶65∶17.5혼합양화고구주작위개질,m(염료)∶m(개질)=1∶20,구마48 h,득도료은정적염료분산액,과립평균립경D50위132 nm.
The micro- nano- sized C.I. Disperse Red 60 was prepared from the corresponding commodity disperse dye by bal mil ing, using zirconia beads as the bal mil medium and sodium lignosulphonate/polynaph?thalenesulphonate as dispersants. The effects of mil ing parameters on the particle size of the dye and its dis?persion stability were investigated. The results showed that mixed- bal mil medium with different diameters was better than that of single diameter of bal , and mixed dispersants excel ed their separate components. Un?der the conditions of the dye amount 20% in the dispersion, mass ratio of the dye/dispersant 1∶1, mass ratio of sodium lignosulphonate CBOS- 4/polynaphthalenesulphonate MF 2∶1, polyol amount 10% in the dispersion (on the mass of dye solution), mixed- bal mil medium of zirconia beads Φ=2 mm/Φ=1 mm/Φ=0.5 mm with mass ratio of 17.5∶65∶17.5, mass ratio of the dye/mil medium 1∶20, and the mil ing time 48 h, a stable dye dispersion was obtained with 132 nm of average particle size D50.