铸坯%钢板%边部裂纹%火焰切割
鑄坯%鋼闆%邊部裂紋%火燄切割
주배%강판%변부렬문%화염절할
casting blank%steel plate%edge crack%flame cutting
铸坯火焰切角轧制后钢板出现严重的边部裂纹,对钢板边部裂纹和铸坯低倍试样进行了分析,发现低倍试样切割面存在密集的裂纹,进一步研究发现这是由于火焰切割造成的,进而推断出,铸坯火焰切角导致钢板边部严重裂纹。
鑄坯火燄切角軋製後鋼闆齣現嚴重的邊部裂紋,對鋼闆邊部裂紋和鑄坯低倍試樣進行瞭分析,髮現低倍試樣切割麵存在密集的裂紋,進一步研究髮現這是由于火燄切割造成的,進而推斷齣,鑄坯火燄切角導緻鋼闆邊部嚴重裂紋。
주배화염절각알제후강판출현엄중적변부렬문,대강판변부렬문화주배저배시양진행료분석,발현저배시양절할면존재밀집적렬문,진일보연구발현저시유우화염절할조성적,진이추단출,주배화염절각도치강판변부엄중렬문。
After cutting the edge of slab by flame, cracks occur on the edge of corresponding steel plates. And the research of slab sample shows that there are serried cracks on the flame cutting section. Further research shows it is due to the flame cutting that form the edge cracks. So it is concluded that the flame cutting on the slab edges resulted the cracks on the edge of plates.