稀土六硼化物%纳米粉末%光吸收
稀土六硼化物%納米粉末%光吸收
희토륙붕화물%납미분말%광흡수
rare-earth hexaborides%nanocrystalline%optical absorption
以稀土氧化物La2 O3和CeO2为稀土源,以NaBH4为硼源在真空环境中通过固相反应成功制备出了分散性好的单相三元LaxCe1?xB6亚微米粉。系统研究了掺杂元素La对CeB6物相,微观结构及光吸收性能的影响。实验结果表明, La元素的掺杂没有改变CeB6的物相和晶体结构,而是无序替代了Ce原子晶位。光吸收结果表明,随着La掺杂量的增加LaxCe1?xB6分散液吸收谷波长从620 nm减小到610 nm出现了蓝移现象。
以稀土氧化物La2 O3和CeO2為稀土源,以NaBH4為硼源在真空環境中通過固相反應成功製備齣瞭分散性好的單相三元LaxCe1?xB6亞微米粉。繫統研究瞭摻雜元素La對CeB6物相,微觀結構及光吸收性能的影響。實驗結果錶明, La元素的摻雜沒有改變CeB6的物相和晶體結構,而是無序替代瞭Ce原子晶位。光吸收結果錶明,隨著La摻雜量的增加LaxCe1?xB6分散液吸收穀波長從620 nm減小到610 nm齣現瞭藍移現象。
이희토양화물La2 O3화CeO2위희토원,이NaBH4위붕원재진공배경중통과고상반응성공제비출료분산성호적단상삼원LaxCe1?xB6아미미분。계통연구료참잡원소La대CeB6물상,미관결구급광흡수성능적영향。실험결과표명, La원소적참잡몰유개변CeB6적물상화정체결구,이시무서체대료Ce원자정위。광흡수결과표명,수착La참잡량적증가LaxCe1?xB6분산액흡수곡파장종620 nm감소도610 nm출현료람이현상。
According to original knowledge, lanthanum hexaboride (LaB6) as an excellent thermionic electron emitter is char-acterized by a low work function, a high emission density, and a high brightness. Recently, much attention has been drawn to its another excellent optical properties: strong light absorption in near infrared rays (NIR), and transparency in visible light (VL), which result from the free electron plasmon resonance. However, up to now the optical properties and syntheses of ternary rare-earth hexaborides have been very rarely reported in the literature. In this paper, ternary LaxCe1?xB6 submicron crystallines are successfully synthesized using a solid-state reaction, in which La2O3 and CeO2 are used as rare-earth sources and NaBH4 as boron sources in a continuous vacuum condition. Effects of La doping content on the LaxCe1?xB6 phase composition, microstructure, and optical absorption properties are investigated by X-ray diffraction, scanning electron microscope (SEM), and transmission electron microscope (TEM). It is found that all the synthesized samples are composed of CaB6-type single-phase alloy with a space group P mˉ3m at the reaction temperature of 1200 ?C held by 2 h. The SEM results indicate that the cubic-shaped ternary LaxCe1?xB6 crystals with a mean size of 200 nm are obtained and the energy dispersive spectrometer results confirm that the La atoms are randomly distributed at the lattice sites of CeB6. High resolution transmission electron microscope images reveal the single-crystalline nature, and the FFT pattern indicates the lattice fringe d = 0.42 nm which agrees well with the (100) crystal plane. EDS analysis of TEM also indicates the La element has been doped into CeB6. And the optical absorption result shows that the absorption valley of CeB6 is 62 nm. With increasing La doping content to x = 0.6 and 0.8, the absorption valleys of La0.6Ce0.4B6 and La0.8Ce0.2B6 decrease to 613 and 610 nm respectively indicating the blueshifts of the wavelength of absorption valley From the view point of practical application, the tunable characteristic of LaxCe1?xB6 may extend the optical applications in improving the e?ciency of organic photovoltaics, replacing the expensive gold and silver nanoparticles, which may have a good usage in optical filters.