中国有色金属学报
中國有色金屬學報
중국유색금속학보
THE CHINESE JOURNAL OF NONFERROUS METALS
2015年
4期
1025-1031
,共7页
刘培生%侯红亮%顷淮斌%王耀奇%张艳苓
劉培生%侯紅亮%頃淮斌%王耀奇%張豔苓
류배생%후홍량%경회빈%왕요기%장염령
多孔材料%泡沫金属%泡沫钛%特性%网状结构
多孔材料%泡沫金屬%泡沫鈦%特性%網狀結構
다공재료%포말금속%포말태%특성%망상결구
porous material%foamed metal%foamed titanium%characteristic%netlike structure
网状泡沫钛属于弹脆性多孔材料,其压缩曲线的平台区为锯齿形,并在总体上呈缓慢增长的趋势;其平台区结束的极限应变较大,且密实化阶段的应力?应变曲线不是那么陡峭。采用浸浆烧结法制备获得了一种孔率在85%~90%之间、孔径分布在1~3 mm之间的网状泡沫钛。结果表明:该泡沫钛制品的热导率随着样品孔率的提高而明显地减小,且总体上具有良好的隔热性能,孔率为87%~89%的试样的室温热导率为0.4~0.8 W/(m·K)。此外,还测试该泡沫钛试样在200~6300 Hz声频范围内的吸声系数,发现其第一共振频率出现在4000 Hz左右,此时试样的吸声系数达到约0.9。
網狀泡沫鈦屬于彈脆性多孔材料,其壓縮麯線的平檯區為鋸齒形,併在總體上呈緩慢增長的趨勢;其平檯區結束的極限應變較大,且密實化階段的應力?應變麯線不是那麽陡峭。採用浸漿燒結法製備穫得瞭一種孔率在85%~90%之間、孔徑分佈在1~3 mm之間的網狀泡沫鈦。結果錶明:該泡沫鈦製品的熱導率隨著樣品孔率的提高而明顯地減小,且總體上具有良好的隔熱性能,孔率為87%~89%的試樣的室溫熱導率為0.4~0.8 W/(m·K)。此外,還測試該泡沫鈦試樣在200~6300 Hz聲頻範圍內的吸聲繫數,髮現其第一共振頻率齣現在4000 Hz左右,此時試樣的吸聲繫數達到約0.9。
망상포말태속우탄취성다공재료,기압축곡선적평태구위거치형,병재총체상정완만증장적추세;기평태구결속적겁한응변교대,차밀실화계단적응력?응변곡선불시나요두초。채용침장소결법제비획득료일충공솔재85%~90%지간、공경분포재1~3 mm지간적망상포말태。결과표명:해포말태제품적열도솔수착양품공솔적제고이명현지감소,차총체상구유량호적격열성능,공솔위87%~89%적시양적실온열도솔위0.4~0.8 W/(m·K)。차외,환측시해포말태시양재200~6300 Hz성빈범위내적흡성계수,발현기제일공진빈솔출현재4000 Hz좌우,차시시양적흡성계수체도약0.9。
The foamed titanium belongs to the elastic-brittle material, and its compression curve has a hackle-like plateau and rise slowly. The terminal strain is quite large when this plateau ends, and the stress?strain curve in the densification stage is not so steep. A sort of reticulated foamed titanium with porosity of 85%?90%and pore diameter of 1?3 mm was prepared by the organic foam impregnating method. The results show that the thermal conductivity decreases markedly with increasing porosity for this foamed titanium, which performs a good heat-insulation. The room-temperature thermal conductivity of the sample with 87%?89%porosity is 0.4?0.8 W/(m·K). In addition, the sound absorption coefficient of this foamed titanium is also measured in 200?6300 Hz, the first resonant frequency occurs at about 4000 Hz, and the sound absorption coefficient reaches up to 0.9.