聚脲%防腐蚀%环氧%改性%钢结构
聚脲%防腐蝕%環氧%改性%鋼結構
취뇨%방부식%배양%개성%강결구
polyurea%anti-corrosion%epoxy%modified%steel structure
为进一步提高聚脲材料的防腐蚀性能,采用环氧改性方法制备了聚脲超重防腐蚀涂料。研究了不同多元醇种类、不同异氰酸酯基(NCO)含量和不同环氧树脂的种类及用量对环氧改性超重防腐蚀聚脲性能的影响。结果表明,环氧改性超重防腐蚀聚脲 A 组分采用聚四氢呋喃(THF)醚多元醇 PTMG-1000与二苯甲烷二异氰酸酯(MDI)合成,NCO 含量16%,环氧树脂 E-44含量10%改性合成,B 组分采用端氨基聚醚 D-2000、T-5000,胺扩链剂 E-100、E-300,环氧树脂 E-44含量15%改性合成制备的环氧改性超重防腐聚脲,具有较好的防腐蚀性能。并且对比研究了采用研制的环氧改性超重防腐蚀聚脲与普通防腐蚀聚脲的性能,结果显示,环氧改性超重防腐蚀聚脲的耐腐性能有显著提升。
為進一步提高聚脲材料的防腐蝕性能,採用環氧改性方法製備瞭聚脲超重防腐蝕塗料。研究瞭不同多元醇種類、不同異氰痠酯基(NCO)含量和不同環氧樹脂的種類及用量對環氧改性超重防腐蝕聚脲性能的影響。結果錶明,環氧改性超重防腐蝕聚脲 A 組分採用聚四氫呋喃(THF)醚多元醇 PTMG-1000與二苯甲烷二異氰痠酯(MDI)閤成,NCO 含量16%,環氧樹脂 E-44含量10%改性閤成,B 組分採用耑氨基聚醚 D-2000、T-5000,胺擴鏈劑 E-100、E-300,環氧樹脂 E-44含量15%改性閤成製備的環氧改性超重防腐聚脲,具有較好的防腐蝕性能。併且對比研究瞭採用研製的環氧改性超重防腐蝕聚脲與普通防腐蝕聚脲的性能,結果顯示,環氧改性超重防腐蝕聚脲的耐腐性能有顯著提升。
위진일보제고취뇨재료적방부식성능,채용배양개성방법제비료취뇨초중방부식도료。연구료불동다원순충류、불동이청산지기(NCO)함량화불동배양수지적충류급용량대배양개성초중방부식취뇨성능적영향。결과표명,배양개성초중방부식취뇨 A 조분채용취사경부남(THF)미다원순 PTMG-1000여이분갑완이이청산지(MDI)합성,NCO 함량16%,배양수지 E-44함량10%개성합성,B 조분채용단안기취미 D-2000、T-5000,알확련제 E-100、E-300,배양수지 E-44함량15%개성합성제비적배양개성초중방부취뇨,구유교호적방부식성능。병차대비연구료채용연제적배양개성초중방부식취뇨여보통방부식취뇨적성능,결과현시,배양개성초중방부식취뇨적내부성능유현저제승。
In order to improve the corrosion resistance of polyurea materials,heavy anti-corrosion polyurea coatings were prepared by epoxy-modification.The effects of different types of polyol,different NCO contents,different types and contents of epoxy resin on the performance of heavy-duty anticorrosion polyurea coatings were studied.The results showed that epoxy-modified anticorrosion polyurea coatings had relatively good corrosion resistance.In epoxy-modified anticorrosion polyurea coatings,the component A was synthesized by poly THF ether polyols PTMG-1000 and MDI,and NCO content was 16%,epoxy resin E-44 content was 10%;the component B was synthesized by terminal amino polyether D-2000 and T-5000,amine chain extender E-100 and E-300,epoxy resin E-44 content was 15%.Performance comparison was made between epoxy-modified anti-corrosion polyurea and general anti-corrosion polyurea,the results showed that the epoxy-modified anti-corrosion polyurea performance was significantly improved.