腐蚀与防护
腐蝕與防護
부식여방호
CORROSION & PROTECTION
2015年
4期
369-372
,共4页
刘成臣%鲁国富%张金奎%王浩伟
劉成臣%魯國富%張金奎%王浩偉
류성신%로국부%장금규%왕호위
合金钢%环境谱%当量关系%腐蚀
閤金鋼%環境譜%噹量關繫%腐蝕
합금강%배경보%당량관계%부식
alloy steel%environment spectrum%equivalent%corrosion
基于某海域舰面停放环境谱,采用30CrMnSiA 材料制备模拟件,在某海域采取悬挂方式开展自然暴露试验的同时在试验室环境下开展了加速腐蚀试验。对腐蚀后试样的失重和疲劳寿命进行了测试,结果表明,30CrMnSiA试验件在当量加速腐蚀试验时间和某海域自然老化时间匹配时,腐蚀失重和疲劳寿命在95%置信度下一致。
基于某海域艦麵停放環境譜,採用30CrMnSiA 材料製備模擬件,在某海域採取懸掛方式開展自然暴露試驗的同時在試驗室環境下開展瞭加速腐蝕試驗。對腐蝕後試樣的失重和疲勞壽命進行瞭測試,結果錶明,30CrMnSiA試驗件在噹量加速腐蝕試驗時間和某海域自然老化時間匹配時,腐蝕失重和疲勞壽命在95%置信度下一緻。
기우모해역함면정방배경보,채용30CrMnSiA 재료제비모의건,재모해역채취현괘방식개전자연폭로시험적동시재시험실배경하개전료가속부식시험。대부식후시양적실중화피로수명진행료측시,결과표명,30CrMnSiA시험건재당량가속부식시험시간화모해역자연노화시간필배시,부식실중화피로수명재95%치신도하일치。
Based on the environmental spectrum of a certain area,30CrMnSiA was used to prepare specimens of bolted lap joints.Part of joints were tested in field accelerated environment corrosion testing was carried out in laboratory .Weight loss and fatigue life were used to evaluate the corrosion degree.The results showed that the weight loss and fatigue life for accelerated corrosion and natural aging corrosion were consistent at the confidence level of 95% in matched time.