酸性硫酸盐光亮镀铜%故障分析%直流母排%温度%阳极
痠性硫痠鹽光亮鍍銅%故障分析%直流母排%溫度%暘極
산성류산염광량도동%고장분석%직류모배%온도%양겁
bright acid sulfate copper plating%fault analysis%direct current bus%temperature%anode
通过10个故障实例,从设备、阳极、镀液成分、电镀温度等4个方面分析了酸性硫酸盐镀铜生产现场出现“电镀电流下降、电压升高”故障的原因,并给出了对应的处理方法,指出了预防类似故障的15个技术要点。
通過10箇故障實例,從設備、暘極、鍍液成分、電鍍溫度等4箇方麵分析瞭痠性硫痠鹽鍍銅生產現場齣現“電鍍電流下降、電壓升高”故障的原因,併給齣瞭對應的處理方法,指齣瞭預防類似故障的15箇技術要點。
통과10개고장실례,종설비、양겁、도액성분、전도온도등4개방면분석료산성류산염도동생산현장출현“전도전류하강、전압승고”고장적원인,병급출료대응적처리방법,지출료예방유사고장적15개기술요점。
The causes of decreasing current with increasing voltage in acid sulfate copper plating were analyzed from devices, anode, bath composition, and plating temperature in terms of 10 fault instances. The corresponding treatment measures were provided. Fifteen technical points to prevent faults were given.