球形件%反复拉深%有限元模拟%近等壁厚成形
毬形件%反複拉深%有限元模擬%近等壁厚成形
구형건%반복랍심%유한원모의%근등벽후성형
spherical part%repetitive deep drawing%finite element simulation%near equal-thick-ness wall forming
提出了球形件反复拉深成形工艺,对该工艺进行了有限元模拟与试验验证。与一次拉深成形工艺进行了对比分析,结果表明:凹模圆角区与法兰区应力状态及大小基本相同,但在球底区,反复拉深时径向应力和周向应力都远小于一次拉深的应力,球底区径向应力和周向应力基本为压应力或很小的拉应力;反复拉深时球底区厚度方向应变明显减小,一次拉深、二次反复拉深、三次反复拉深成形的制品最薄点减薄率分别为0.189、0.122、0.049,三次反复拉深可实现近等壁厚制品的拉深成形。该工艺与筒底冷校形工艺相结合,可实现近等壁厚深筒形零件的拉深成形。
提齣瞭毬形件反複拉深成形工藝,對該工藝進行瞭有限元模擬與試驗驗證。與一次拉深成形工藝進行瞭對比分析,結果錶明:凹模圓角區與法蘭區應力狀態及大小基本相同,但在毬底區,反複拉深時徑嚮應力和週嚮應力都遠小于一次拉深的應力,毬底區徑嚮應力和週嚮應力基本為壓應力或很小的拉應力;反複拉深時毬底區厚度方嚮應變明顯減小,一次拉深、二次反複拉深、三次反複拉深成形的製品最薄點減薄率分彆為0.189、0.122、0.049,三次反複拉深可實現近等壁厚製品的拉深成形。該工藝與筒底冷校形工藝相結閤,可實現近等壁厚深筒形零件的拉深成形。
제출료구형건반복랍심성형공예,대해공예진행료유한원모의여시험험증。여일차랍심성형공예진행료대비분석,결과표명:요모원각구여법란구응력상태급대소기본상동,단재구저구,반복랍심시경향응력화주향응력도원소우일차랍심적응력,구저구경향응력화주향응력기본위압응력혹흔소적랍응력;반복랍심시구저구후도방향응변명현감소,일차랍심、이차반복랍심、삼차반복랍심성형적제품최박점감박솔분별위0.189、0.122、0.049,삼차반복랍심가실현근등벽후제품적랍심성형。해공예여통저랭교형공예상결합,가실현근등벽후심통형령건적랍심성형。
A new repetitive deep drawing forming of spherical parts was presented and finite element sim-ulation and experiments were carried out.The stress state and values were almost equal in the flange area and in the circle-corners compared with once deep drawing forming,but in the ball bottom area the radial stresses and circumferential stresses were pressure stresses or small tensile stresses,which were much less than that in once deep drawing.The thinning strain of parts is reduced evidently in the ball bottom area for repetitive deep drawing.The thinning rate of forming parts in thinnest point for once deep drawing,2-time deep drawing and 3-time deep drawing are as 0.189,0.122,0.049 respectively.The thinning strain is very small in the 3-time repetitive deep drawing,which realizes near equal-thickness wall forming.Combined with the bottom cold sizing technology,the technology can realize the forming of deep cup with uniform thickness.