201冷轧板%锈蚀缺陷%非金属夹杂物%氯离子
201冷軋闆%鏽蝕缺陷%非金屬夾雜物%氯離子
201랭알판%수식결함%비금속협잡물%록리자
201 cold rolling sheet%rust corrosion defects%nonmetal inclusion%chloridion
针对201不锈钢冷轧板表面锈蚀缺陷，选取试样进行分析，发现使用环境中存在的氯离子和材料自身非金属夹杂物是导致锈蚀出现的主要原因，并提出了相应的控制措施。
針對201不鏽鋼冷軋闆錶麵鏽蝕缺陷，選取試樣進行分析，髮現使用環境中存在的氯離子和材料自身非金屬夾雜物是導緻鏽蝕齣現的主要原因，併提齣瞭相應的控製措施。
침대201불수강랭알판표면수식결함，선취시양진행분석，발현사용배경중존재적록리자화재료자신비금속협잡물시도치수식출현적주요원인，병제출료상응적공제조시。
Regarding to rust corrosion on the surface of 201 stainless steel cold rolling sheet, specimen has been selected and analyzed, it found that chloridion existing in operational ciucumstance and nonmetal inclusions of material were the main cause to result in rust corrosion, further corresponding control measures have been brought up.