绝缘材料
絕緣材料
절연재료
INSULATING MATERIALS
2015年
6期
68-71
,共4页
于钦学%郑文杰%任文娥%钟力生
于欽學%鄭文傑%任文娥%鐘力生
우흠학%정문걸%임문아%종력생
变频电机%电磁线绝缘%电老化%显微镜观察%能谱分析
變頻電機%電磁線絕緣%電老化%顯微鏡觀察%能譜分析
변빈전궤%전자선절연%전노화%현미경관찰%능보분석
inverter-fed motor%electromagnetic wire insulation%electrical ageing%electron microscope%energy spectrum analysis
通过对变频电机用绝缘电磁线进行高频脉冲电老化试验,研究了绝缘电磁线的电老化寿命及其变化规律。采用电子能谱仪和显微镜对绝缘电磁线表面在电老化过程中的析出物进行了成分分析和形貌表征。结果表明:绝缘电磁线在施加一定电压条件下会出现局部放电,其寿命随施加电压的增加呈指数式衰减,在电老化过程中电磁线绝缘表面有白色析出物质,对试样表面析出物进行能谱分析发现C、O、Mg、Si、Ca增加较多,击穿点周围C、F、Cu元素含量大幅度增加。新试样表面平坦且没有杂质,而经过电老化后的电磁线试样表面团聚物堆积、凹凸不平。
通過對變頻電機用絕緣電磁線進行高頻脈遲電老化試驗,研究瞭絕緣電磁線的電老化壽命及其變化規律。採用電子能譜儀和顯微鏡對絕緣電磁線錶麵在電老化過程中的析齣物進行瞭成分分析和形貌錶徵。結果錶明:絕緣電磁線在施加一定電壓條件下會齣現跼部放電,其壽命隨施加電壓的增加呈指數式衰減,在電老化過程中電磁線絕緣錶麵有白色析齣物質,對試樣錶麵析齣物進行能譜分析髮現C、O、Mg、Si、Ca增加較多,擊穿點週圍C、F、Cu元素含量大幅度增加。新試樣錶麵平坦且沒有雜質,而經過電老化後的電磁線試樣錶麵糰聚物堆積、凹凸不平。
통과대변빈전궤용절연전자선진행고빈맥충전노화시험,연구료절연전자선적전노화수명급기변화규률。채용전자능보의화현미경대절연전자선표면재전노화과정중적석출물진행료성분분석화형모표정。결과표명:절연전자선재시가일정전압조건하회출현국부방전,기수명수시가전압적증가정지수식쇠감,재전노화과정중전자선절연표면유백색석출물질,대시양표면석출물진행능보분석발현C、O、Mg、Si、Ca증가교다,격천점주위C、F、Cu원소함량대폭도증가。신시양표면평탄차몰유잡질,이경과전노화후적전자선시양표면단취물퇴적、요철불평。
The electrical ageing life and its change rule of electromagnetic wire insulation for inverter-fed motor were studied through high frequency pulse electrical ageing test. The composition and morphology of the precipitates appeared on the eletromagnetic wire insulation surface during electrical ageing were analyzed by electron spectroscopy and microscope. The results show that the partial discharge would appear when electromagnetic wire is applied certain voltage, and its life decreases exponentially with the increase of applied voltage. Some white precipitates are found on the electromagnetic wire insulation surface. It is found that the C, O, Mg, Si, and Ca element content in precipitates increase a lot through analyzing the energy spectra of samples, and the C, F, and Cu element content increase significantly around the breakdown point. The new sample has smooth surface and no impurities, and the surface of electrical ageing sample is uneven and accumulated with agglomerate.