工程科学学报
工程科學學報
공정과학학보
Journal of University of Science and Technology Beijing
2015年
6期
764-770
,共7页
曹晖%尹聿海%肖玲%王冬%杨洲
曹暉%尹聿海%肖玲%王鼕%楊洲
조휘%윤율해%초령%왕동%양주
聚合物网络%胆甾相液晶%薄膜%电光性能%聚合温度%紫外光照射
聚閤物網絡%膽甾相液晶%薄膜%電光性能%聚閤溫度%紫外光照射
취합물망락%담치상액정%박막%전광성능%취합온도%자외광조사
polymer networks%cholesteric liquid crystals%thin films%electro-optical properties%curing temperature%ultraviolet irradiation
选用1,4-双[4-(6-丙烯酰氧基己氧基)苯甲酰氧基]-2-甲苯(C6M)/(S)-4'-(2-甲基丁基)-4-联苯腈(CB15)/安息香二甲醚(IRG651)/SLC1717复合体系,通过紫外光聚合诱导相分离法制备了反式聚合物稳定胆甾相织构(R-PSCT)膜.研究了聚合温度和紫外光辐照度对所制备的R-PSCT膜电光性能的影响.随着聚合温度的升高或紫外光辐照度的减小,R-PSCT膜的驱动电压、对比度和开态响应时间减小,而关态响应时间增大.在聚合温度为293 K和紫外光辐照度为0.75 mW·cm-2时,所制备的R-PSCT膜具有较佳的电光性能.
選用1,4-雙[4-(6-丙烯酰氧基己氧基)苯甲酰氧基]-2-甲苯(C6M)/(S)-4'-(2-甲基丁基)-4-聯苯腈(CB15)/安息香二甲醚(IRG651)/SLC1717複閤體繫,通過紫外光聚閤誘導相分離法製備瞭反式聚閤物穩定膽甾相織構(R-PSCT)膜.研究瞭聚閤溫度和紫外光輻照度對所製備的R-PSCT膜電光性能的影響.隨著聚閤溫度的升高或紫外光輻照度的減小,R-PSCT膜的驅動電壓、對比度和開態響應時間減小,而關態響應時間增大.在聚閤溫度為293 K和紫外光輻照度為0.75 mW·cm-2時,所製備的R-PSCT膜具有較佳的電光性能.
선용1,4-쌍[4-(6-병희선양기기양기)분갑선양기]-2-갑분(C6M)/(S)-4'-(2-갑기정기)-4-련분정(CB15)/안식향이갑미(IRG651)/SLC1717복합체계,통과자외광취합유도상분리법제비료반식취합물은정담치상직구(R-PSCT)막.연구료취합온도화자외광복조도대소제비적R-PSCT막전광성능적영향.수착취합온도적승고혹자외광복조도적감소,R-PSCT막적구동전압、대비도화개태향응시간감소,이관태향응시간증대.재취합온도위293 K화자외광복조도위0.75 mW·cm-2시,소제비적R-PSCT막구유교가적전광성능.
ABSTRACT Reverse-mode polymer-stabilized cholesteric texture ( R-PSCT) films were prepared from ultraviolet polymerization-in-duced phase separation in a mixture of 1,4-di[4-(6-acryloyloxyhexyloxy) benzoyloxy]-2-methylbenzene(C6M)/ (S)-4’-(2-methyl-butyl)biphenyl-4-carbonitrile(CB15)/2,2-dimethopxy-1,2-diphenyl-ethanone(IRG651)/SLC1717. The effects of curing temperature and ultraviolet ( UV) irradiance on the electro-optical properties of R-PSCT films were studied. When the curing temperature increases or the ultraviolet irradiance decreases, the driving voltage, the contrast ratio and the on-state response time decrease, but the off-state response time increases. The R-PSCT film prepared at a curing temperature of 293 K and an ultraviolet irradiance of 0.75 mW·cm-2 has better electro-optical properties.