分级%配比%粒度分布%抗拉强度%杯突值
分級%配比%粒度分佈%抗拉彊度%杯突值
분급%배비%립도분포%항랍강도%배돌치
grading%mixed in proportion%particle size distribution%tensile strength%cupping values
钼粉的粒度对钼制品性能的影响已有较多研究,而与钼粉粒度分级技术对钼制品深加工性能影响的相关报道较少。研究选用了3种不同粒度的钼粉按照Ⅰ级(FSSS≥3.5μm)、Ⅱ级(FSSS:2.5~3.5μm)、Ⅲ级(FSSS≤2.5μm)3个级别进行分级,并将分级钼粉按Ⅰ级钼粉10%,Ⅱ级钼粉80%,Ⅲ级钼粉10%的比例进行配比。通过压型和烧结将原料钼粉、分级钼粉和配比钼粉分别加工成钼板坯,并将钼板坯轧制和冲压成钼箔、钼圆片。检测了钼箔的抗拉强度和杯突值,并统计分析了钼圆片的成品率。试验证明,在钼制品抗拉强度、胀形成形性能以及成品率方面,配比钼粉均优于单一粒度组成的钼粉和未分级的普通钼粉。
鉬粉的粒度對鉬製品性能的影響已有較多研究,而與鉬粉粒度分級技術對鉬製品深加工性能影響的相關報道較少。研究選用瞭3種不同粒度的鉬粉按照Ⅰ級(FSSS≥3.5μm)、Ⅱ級(FSSS:2.5~3.5μm)、Ⅲ級(FSSS≤2.5μm)3箇級彆進行分級,併將分級鉬粉按Ⅰ級鉬粉10%,Ⅱ級鉬粉80%,Ⅲ級鉬粉10%的比例進行配比。通過壓型和燒結將原料鉬粉、分級鉬粉和配比鉬粉分彆加工成鉬闆坯,併將鉬闆坯軋製和遲壓成鉬箔、鉬圓片。檢測瞭鉬箔的抗拉彊度和杯突值,併統計分析瞭鉬圓片的成品率。試驗證明,在鉬製品抗拉彊度、脹形成形性能以及成品率方麵,配比鉬粉均優于單一粒度組成的鉬粉和未分級的普通鉬粉。
목분적립도대목제품성능적영향이유교다연구,이여목분립도분급기술대목제품심가공성능영향적상관보도교소。연구선용료3충불동립도적목분안조Ⅰ급(FSSS≥3.5μm)、Ⅱ급(FSSS:2.5~3.5μm)、Ⅲ급(FSSS≤2.5μm)3개급별진행분급,병장분급목분안Ⅰ급목분10%,Ⅱ급목분80%,Ⅲ급목분10%적비례진행배비。통과압형화소결장원료목분、분급목분화배비목분분별가공성목판배,병장목판배알제화충압성목박、목원편。검측료목박적항랍강도화배돌치,병통계분석료목원편적성품솔。시험증명,재목제품항랍강도、창형성형성능이급성품솔방면,배비목분균우우단일립도조성적목분화미분급적보통목분。
TThis paper studied the effect of grading technology on the performance of molybdenum products deep processing. We graded three different molybdenum powders into level I(FSSS≥3.5μm), level II (FSSS:2.5~3.5μm) and level III (FSSS≤2.5μm). Ratio operations were performed on the graded M powder according to the proportions of level I 10%, level II 80%and level III 10%. The ungraded M powder, graded M powder and mixed M powder were respectively processed into M slabs, foils and wafers by sintering, rolling and stamping. The tensile strength and the cupping values of Mo-foil were tested and the yield rates of the Mo-discs were calculated. The experiments proved that, the m products out of mixed Molybdenum powder according to the set ratio demonstrates better properties in terms of tensile strength, formability and finished Bulge rates comparing with those of the single particle sized M powder and ungraded M powder.