膨润土%海藻酸钠%乳化-内部凝胶化%2,4-D%微球
膨潤土%海藻痠鈉%乳化-內部凝膠化%2,4-D%微毬
팽윤토%해조산납%유화-내부응효화%2,4-D%미구
bentonite%sodium alginate%emulsification/internal gelation%2,4-D%microspheres
以膨润土为改性剂,纳米碳酸钙为交联剂,2,4-二氯苯氧乙酸(2,4-D)为模型药物,采用乳化-内部凝胶法制备了2,4-D/膨润土/海藻酸钠复合微球,并利用光学显微镜和激光粒度仪对微球的形貌和平均粒径分别进行了表征,对乳化-内部凝胶化工艺(油水体积比、乳化剂用量、纳米碳酸钙用量以及搅拌速度)对微球的形貌、平均粒径和载药量的影响进行了探究.结果表明,当油水体积比为5∶1,乳化剂用量为石蜡体积分数的1%,纳米碳酸钙为0.2 g,搅拌速度为400 r/min时,载药微球的粒径分布均一、球形度较好,其平均粒径为640.57μm,载药量为15.66%.这种复合材料可以作为农药载体,有望应用于缓释农药领域.
以膨潤土為改性劑,納米碳痠鈣為交聯劑,2,4-二氯苯氧乙痠(2,4-D)為模型藥物,採用乳化-內部凝膠法製備瞭2,4-D/膨潤土/海藻痠鈉複閤微毬,併利用光學顯微鏡和激光粒度儀對微毬的形貌和平均粒徑分彆進行瞭錶徵,對乳化-內部凝膠化工藝(油水體積比、乳化劑用量、納米碳痠鈣用量以及攪拌速度)對微毬的形貌、平均粒徑和載藥量的影響進行瞭探究.結果錶明,噹油水體積比為5∶1,乳化劑用量為石蠟體積分數的1%,納米碳痠鈣為0.2 g,攪拌速度為400 r/min時,載藥微毬的粒徑分佈均一、毬形度較好,其平均粒徑為640.57μm,載藥量為15.66%.這種複閤材料可以作為農藥載體,有望應用于緩釋農藥領域.
이팽윤토위개성제,납미탄산개위교련제,2,4-이록분양을산(2,4-D)위모형약물,채용유화-내부응효법제비료2,4-D/팽윤토/해조산납복합미구,병이용광학현미경화격광립도의대미구적형모화평균립경분별진행료표정,대유화-내부응효화공예(유수체적비、유화제용량、납미탄산개용량이급교반속도)대미구적형모、평균립경화재약량적영향진행료탐구.결과표명,당유수체적비위5∶1,유화제용량위석사체적분수적1%,납미탄산개위0.2 g,교반속도위400 r/min시,재약미구적립경분포균일、구형도교호,기평균립경위640.57μm,재약량위15.66%.저충복합재료가이작위농약재체,유망응용우완석농약영역.
2,4-D/bentonite/sodium alginate composite microspheres were prepared by emulsification/internal gelation method choosing bentonite as modifier, nano-calcium carbonate as crosslinking agent and 2,4-Dichlorophenoxyacetic acid (2,4-D) was as model drug.Morphologies and average particle size of composite microspheres were characterized by optical microscope and laser particle size analyzer.And the effect of emulsification/internal gelation process ( various oil-water ratio, mass rations of emulsifier and nano-calcium carbonate and stirring speed) on morphologies, average particle size and loading con-tent (LC) of microspheres were investigated.The result showed that while oil-water ratio was 5∶1, mass ratio of emulsifier to paraffin was 1%, nano-calcium carbonate dosage was 0.2 g, stirring speed was 400 r/min, the LC of 2,4-D was 15.66%and average particle size was 640.57μm.This composite materi-al can be used as pesticide carrier and is expected to be applied in the field of pesticide slow-release.