杜金松%曹建国%李宁%赵琬倩%申开智
杜金鬆%曹建國%李寧%趙琬倩%申開智
두금송%조건국%리저%조완천%신개지
动态保压%诱导%聚乙烯%串晶%自增强
動態保壓%誘導%聚乙烯%串晶%自增彊
동태보압%유도%취을희%천정%자증강
dynamic packing injection molding(DPIM)%induced%PE%shish-kebab%self-enhancement
采用自制的动态保压注射成型(DPIM)装置,向中等分子量的 HDPE 中添加高、低分子量聚乙烯(HMWPE、LMWPE)双重诱导成型自增强串晶的组织与性能影响进行研究.实验表明,在双重诱导和采用 DPIM 装置下,试样产生了大量的串晶结构,在160℃动态保压注射试样的拉伸强度为111.6 MPa,是其 HDPE 纯料静态试样拉伸强度24.5 MPa 的4.56倍,提高了355.5%;通过 WAXD、DSC 和 SEM 测试可知,在 DPIM 下,试样产生互锁紧密的串晶结构;高分子量聚乙烯的加入有利于串晶脊纤维晶体的生成,低分子量聚乙烯的加入有利于片晶生长增厚,从而使得串晶结构更完善.
採用自製的動態保壓註射成型(DPIM)裝置,嚮中等分子量的 HDPE 中添加高、低分子量聚乙烯(HMWPE、LMWPE)雙重誘導成型自增彊串晶的組織與性能影響進行研究.實驗錶明,在雙重誘導和採用 DPIM 裝置下,試樣產生瞭大量的串晶結構,在160℃動態保壓註射試樣的拉伸彊度為111.6 MPa,是其 HDPE 純料靜態試樣拉伸彊度24.5 MPa 的4.56倍,提高瞭355.5%;通過 WAXD、DSC 和 SEM 測試可知,在 DPIM 下,試樣產生互鎖緊密的串晶結構;高分子量聚乙烯的加入有利于串晶脊纖維晶體的生成,低分子量聚乙烯的加入有利于片晶生長增厚,從而使得串晶結構更完善.
채용자제적동태보압주사성형(DPIM)장치,향중등분자량적 HDPE 중첨가고、저분자량취을희(HMWPE、LMWPE)쌍중유도성형자증강천정적조직여성능영향진행연구.실험표명,재쌍중유도화채용 DPIM 장치하,시양산생료대량적천정결구,재160℃동태보압주사시양적랍신강도위111.6 MPa,시기 HDPE 순료정태시양랍신강도24.5 MPa 적4.56배,제고료355.5%;통과 WAXD、DSC 화 SEM 측시가지,재 DPIM 하,시양산생호쇄긴밀적천정결구;고분자량취을희적가입유리우천정척섬유정체적생성,저분자량취을희적가입유리우편정생장증후,종이사득천정결구경완선.
The influence of self-enhancement and shish-kebab of the middling-HDPE added high molecular weight PE and low molecular weight PE was studied by using the self-designed and self-made dynamic packing injection molding (DPIM) equipment.Testing results show that tensile strength of dynamic sample was 1 1 1.6 MPa at 1 60 ℃,which was 4.56 times as high as the static one (24.2 MPa)and approximately increased by 355.5%;it was known that,from the test results of differential scanning calorimetry(DSC),scanning electron microscopy(SEM)and wide-angle X-ray diffraction (WAXD),the interlocking structure of shish-kebab was generated under the acts of DPIM.Adding high molecular weight PE can be beneficial to the formation of shish-kebab spine fiber crystal and the thickness of lamellar crystal was benefit from adding low molecular,so as to improve the property of shish-kebab.