金属矿山
金屬礦山
금속광산
METAL MINE
2015年
7期
64-68
,共5页
李玄武%张亚辉%雷治武%吴安平%李立%洪欢欢
李玄武%張亞輝%雷治武%吳安平%李立%洪歡歡
리현무%장아휘%뢰치무%오안평%리립%홍환환
柠檬酸%改性淀粉%络合剂%抑制剂%铜镍硫化矿%含镁脉石矿物
檸檬痠%改性澱粉%絡閤劑%抑製劑%銅鎳硫化礦%含鎂脈石礦物
저몽산%개성정분%락합제%억제제%동얼류화광%함미맥석광물
Citric acid%Modified starch%Complexing agent%Inhibitors%Copper-nickel sulfide ore%Mg-bearing gangue
金川镍矿石所含Cu2+、Ni2+对矿石中大量的含镁硅酸盐脉石矿物有较强的活化作用,导致镍铜混合精矿MgO含量较高,Ni、Cu品位难以提高。为实现矿山的提质降镁目标,在柠檬酸-改性淀粉药剂体系下进行了选矿试验。结果表明,在磨矿细度为-0.074 mm占90.12%条件下,采用1粗2精3扫、中矿顺序返回流程,可取得Ni、Cu品位分别为9.03%、5.18%,MgO含量6.18%,Ni、Cu回收率分别为85.30%、72.82%的镍铜混合精矿。与模拟现场工艺的实验室试验指标比较,精矿Ni、Cu品位分别提高了0.28、0.07个百分点,精矿Ni、Cu回收率分别提高了3.41、1.04个百分点,MgO含量下降了0.58个百分点。因此,在富含镁硅酸盐脉石矿物的铜镍硫化矿石的浮选中,柠檬酸-改性淀粉具有显著的提质降镁效果。
金川鎳礦石所含Cu2+、Ni2+對礦石中大量的含鎂硅痠鹽脈石礦物有較彊的活化作用,導緻鎳銅混閤精礦MgO含量較高,Ni、Cu品位難以提高。為實現礦山的提質降鎂目標,在檸檬痠-改性澱粉藥劑體繫下進行瞭選礦試驗。結果錶明,在磨礦細度為-0.074 mm佔90.12%條件下,採用1粗2精3掃、中礦順序返迴流程,可取得Ni、Cu品位分彆為9.03%、5.18%,MgO含量6.18%,Ni、Cu迴收率分彆為85.30%、72.82%的鎳銅混閤精礦。與模擬現場工藝的實驗室試驗指標比較,精礦Ni、Cu品位分彆提高瞭0.28、0.07箇百分點,精礦Ni、Cu迴收率分彆提高瞭3.41、1.04箇百分點,MgO含量下降瞭0.58箇百分點。因此,在富含鎂硅痠鹽脈石礦物的銅鎳硫化礦石的浮選中,檸檬痠-改性澱粉具有顯著的提質降鎂效果。
금천얼광석소함Cu2+、Ni2+대광석중대량적함미규산염맥석광물유교강적활화작용,도치얼동혼합정광MgO함량교고,Ni、Cu품위난이제고。위실현광산적제질강미목표,재저몽산-개성정분약제체계하진행료선광시험。결과표명,재마광세도위-0.074 mm점90.12%조건하,채용1조2정3소、중광순서반회류정,가취득Ni、Cu품위분별위9.03%、5.18%,MgO함량6.18%,Ni、Cu회수솔분별위85.30%、72.82%적얼동혼합정광。여모의현장공예적실험실시험지표비교,정광Ni、Cu품위분별제고료0.28、0.07개백분점,정광Ni、Cu회수솔분별제고료3.41、1.04개백분점,MgO함량하강료0.58개백분점。인차,재부함미규산염맥석광물적동얼류화광석적부선중,저몽산-개성정분구유현저적제질강미효과。
MgO content in the nickel-copper mixed concentrate is too high since Cu2+ and Ni2+ ions of Jinchuan nickel ore can strongly activate a large amount of Mg-containing silicate gangue minerals,and the grade of Ni and Cu is difficult to be improved. To achieve the goal of decreasing magnesium and improving quality,the dressing test was carried out under the rea-gent system of citric acid-modified starch combination. The results showed that,at the grinding fineness of 90. 12% -0. 074 mm,through the closed-circuit process of one roughing-two cleaning-three scavenging,and middlings returning in proper order into the flow,the final copper-nickel mixed concentrate with Ni grade of 9. 03%,Cu grade of 5. 18%,MgO content of 6. 18%, nickel recovery of 85. 30%,copper reovery of 72. 82% was obtained. Compared with the laboratory test index of simulating in-situ process, concentrate grade of Ni,Cu is increased by 0. 28 and 0. 07 percentage points respectively,concentrate recovery rate of Ni,Cu is increased by 3. 41 and 1. 04 percentage points respectively,and content of MgO drops 0. 58 percentage points. Therefore,citric acid-modified starch can significantly decrease magnesium content and improve the quality of nickel-copper mixed concentrate in copper-nickel sulfide ore,which is rich in magnesium silicate gangue minerals,flotation process.