合成向列液晶单体:4-((4-烯丙氧基)苯甲酰氧基)苯基-4-氟苯甲酸)酯(M1)和非液晶手性交联剂:双(4-((4-烯丙氧基)苯甲酰氧基)异山梨醇酯)(MC).按不同比例将M1和MC 接枝共聚到聚甲基含氢硅氧烷上,得到含氟手性液晶弹性体PI~PVIII.用红外光谱、核磁共振表征单体和聚合物结构,用差示扫描量热仪、热失重仪、偏光显微镜及X射线衍射等手段研究其液晶性能.结果表明,含氟类短而硬的液晶基元更易被手性诱导,出现性能优异的胆甾相.其中,PI为向列型液晶,PII~PVII为出现油丝和Grandjean织构的胆甾型液晶,PVIII没有液晶性.弹性体玻璃化转变温度随着手性交联剂含量的增加先增大后减小,熔点和清亮点均呈下降趋势.所合成的液晶弹性体热稳定性好,质量损失5%时的热失重温度均在300℃以上.
閤成嚮列液晶單體:4-((4-烯丙氧基)苯甲酰氧基)苯基-4-氟苯甲痠)酯(M1)和非液晶手性交聯劑:雙(4-((4-烯丙氧基)苯甲酰氧基)異山梨醇酯)(MC).按不同比例將M1和MC 接枝共聚到聚甲基含氫硅氧烷上,得到含氟手性液晶彈性體PI~PVIII.用紅外光譜、覈磁共振錶徵單體和聚閤物結構,用差示掃描量熱儀、熱失重儀、偏光顯微鏡及X射線衍射等手段研究其液晶性能.結果錶明,含氟類短而硬的液晶基元更易被手性誘導,齣現性能優異的膽甾相.其中,PI為嚮列型液晶,PII~PVII為齣現油絲和Grandjean織構的膽甾型液晶,PVIII沒有液晶性.彈性體玻璃化轉變溫度隨著手性交聯劑含量的增加先增大後減小,鎔點和清亮點均呈下降趨勢.所閤成的液晶彈性體熱穩定性好,質量損失5%時的熱失重溫度均在300℃以上.
합성향렬액정단체:4-((4-희병양기)분갑선양기)분기-4-불분갑산)지(M1)화비액정수성교련제:쌍(4-((4-희병양기)분갑선양기)이산리순지)(MC).안불동비례장M1화MC 접지공취도취갑기함경규양완상,득도함불수성액정탄성체PI~PVIII.용홍외광보、핵자공진표정단체화취합물결구,용차시소묘량열의、열실중의、편광현미경급X사선연사등수단연구기액정성능.결과표명,함불류단이경적액정기원경역피수성유도,출현성능우이적담치상.기중,PI위향렬형액정,PII~PVII위출현유사화Grandjean직구적담치형액정,PVIII몰유액정성.탄성체파리화전변온도수착수성교련제함량적증가선증대후감소,용점화청량점균정하강추세.소합성적액정탄성체열은정성호,질량손실5%시적열실중온도균재300℃이상.
Nematic monomer: 4-(4-(allyloxy )benzoyloxy )phenyl 4-fluorobenzoate (M1 )and non-liquid crystalline crosslinking agent: bis ((4-(4-allyloxy)benzoyloxy)isosorbide benzoate) (MC ) were synthesized. M1 and MC with different proportions reacted with polymethylhydrosiloxane and chiral liquid crystalline elastomers containing fluorine PI-PVIII were got.The chemical structures and mesomorphic properties of monomers and elastomers were studied by means of FT-IR, 1 H NMR, POM, DSC, TGA and X-ray.The experiment results showed that short-hard liquid crystal elements containing fluorine could be induced into cholesteric phase with wonderful properties.PI presented nematic phase and PII-PVII displayed cholesteric phase with oily-streak and Grandjean texture.PVIII did not have any liquid crystalline properties. The glass-transition temperature increased first and then decreased, whereas both the melting point and clearing point decreased.The synthesized liquid crystal elastomers had good thermal stability, and the thermal weight loss temperature was greater than 300℃with only 5%weight lost.