中国涂料
中國塗料
중국도료
CHINA PAINT
2015年
7期
55-58
,共4页
莫立新%张卫国%崔显林%王同良%成建强
莫立新%張衛國%崔顯林%王同良%成建彊
막립신%장위국%최현림%왕동량%성건강
水成膜消防泡沫%船舶甲板涂料%颜色%环氧%聚氨酯
水成膜消防泡沫%船舶甲闆塗料%顏色%環氧%聚氨酯
수성막소방포말%선박갑판도료%안색%배양%취안지
aqueous iflm forming foam%coatings for ship deck%pigment%epoxy resin%polyurethane
用数字显微镜对水成膜消防泡沫对环氧、聚氨酯甲板涂料的变色影响进行了研究。未经老化的环氧涂料涂膜致密，耐消防泡沫性能较好。老化10个月以上的环氧涂料，表面产生明显老化现象，耐消防泡沫性能大大下降，表面变白并产生细裂纹。
用數字顯微鏡對水成膜消防泡沫對環氧、聚氨酯甲闆塗料的變色影響進行瞭研究。未經老化的環氧塗料塗膜緻密，耐消防泡沫性能較好。老化10箇月以上的環氧塗料，錶麵產生明顯老化現象，耐消防泡沫性能大大下降，錶麵變白併產生細裂紋。
용수자현미경대수성막소방포말대배양、취안지갑판도료적변색영향진행료연구。미경노화적배양도료도막치밀，내소방포말성능교호。노화10개월이상적배양도료，표면산생명현노화현상，내소방포말성능대대하강，표면변백병산생세렬문。
The effect of aqueous iflm forming foam on the discoloration of epoxy and polyurethane deck coatings was researched with the digital microscope. The iflm of the epoxy coatings was compact before aging and had preferable AFFF resistance. But after the epoxy coatings were aged for 10 months, aging phenomenon occurred obviously on the surfaces, the AFFF resistance declined signiifcantly and the surface was whitened and with ifne cracks.