徐松%冯兵%何铁祥%胡波涛%吴欣强
徐鬆%馮兵%何鐵祥%鬍波濤%吳訢彊
서송%풍병%하철상%호파도%오흔강
合金涂层%土壤腐蚀%电化学腐蚀%高速电弧喷涂
閤金塗層%土壤腐蝕%電化學腐蝕%高速電弧噴塗
합금도층%토양부식%전화학부식%고속전호분도
alloy coating%soil corrosion%electrochemical corrosion%high-speed arc spraying
目的:研究Al,AlSi,NiAl,316L不锈钢四种合金涂层在变电站土壤及其溶液中的腐蚀行为。方法采用高速电弧喷涂方法在Q235钢表面上分别制备纯Al,AlSi,NiAl,316L不锈钢合金涂层,通过对四种涂层钢在湖南220 kV毛家塘变电站中进行埋样和土壤溶液里的电化学实验,研究四种涂层在变电站土壤及其溶液中的耐蚀性能,并利用扫描电子显微镜(SEM)和X射线电子能谱(EDS)对埋样的腐蚀产物进行观察和分析。结果 AlSi涂层具有最好的耐土壤腐蚀性,其次是NiAl涂层和316L不锈钢涂层,而纯铝涂层长时间埋地容易鼓泡,耐土壤腐蚀性不佳。结论四种合金涂层显著提高了Q235钢的耐蚀性,可用于接地网材料防腐。
目的:研究Al,AlSi,NiAl,316L不鏽鋼四種閤金塗層在變電站土壤及其溶液中的腐蝕行為。方法採用高速電弧噴塗方法在Q235鋼錶麵上分彆製備純Al,AlSi,NiAl,316L不鏽鋼閤金塗層,通過對四種塗層鋼在湖南220 kV毛傢塘變電站中進行埋樣和土壤溶液裏的電化學實驗,研究四種塗層在變電站土壤及其溶液中的耐蝕性能,併利用掃描電子顯微鏡(SEM)和X射線電子能譜(EDS)對埋樣的腐蝕產物進行觀察和分析。結果 AlSi塗層具有最好的耐土壤腐蝕性,其次是NiAl塗層和316L不鏽鋼塗層,而純鋁塗層長時間埋地容易鼓泡,耐土壤腐蝕性不佳。結論四種閤金塗層顯著提高瞭Q235鋼的耐蝕性,可用于接地網材料防腐。
목적:연구Al,AlSi,NiAl,316L불수강사충합금도층재변전참토양급기용액중적부식행위。방법채용고속전호분도방법재Q235강표면상분별제비순Al,AlSi,NiAl,316L불수강합금도층,통과대사충도층강재호남220 kV모가당변전참중진행매양화토양용액리적전화학실험,연구사충도층재변전참토양급기용액중적내식성능,병이용소묘전자현미경(SEM)화X사선전자능보(EDS)대매양적부식산물진행관찰화분석。결과 AlSi도층구유최호적내토양부식성,기차시NiAl도층화316L불수강도층,이순려도층장시간매지용역고포,내토양부식성불가。결론사충합금도층현저제고료Q235강적내식성,가용우접지망재료방부。
ABSTRACT:Objective To investigate the corrosion behaviors of four alloy coatings (Al, AlSi, NiAl, 316L) samples in the soil and soil solution of transformer substation. Methods Pure Al coating, AlSi alloy coating, NiAl alloy coating and 316L stainless steel coating were prepared on the surface of Q235 steel by high-speed arc spraying technology. The corrosion resistance of the four sprayed alloy coatings in the soil and soil solution of the Maojiatang 220kV transformer substation in Hunan was studied by buried specimens and electrochemical test. The corrosion products of the buried specimens were observed and analyzed by scanning electron microscopy(SEM)and electron diffraction spectra (EDS). Results The results showed that AlSi coating had the best corrosion resistance among the four sprayed alloy coatings, followed by NiA1 and stainless steel coating,and the Al coating was easily bouffant after buried for a long time in theunderground, so that the corrosion resistance was not good. Conclusion The corrosion resistance of steel Q235 was significantly improved by the four sprayed alloy coatings, and the coated steel could be applied in protection of grounding grid materials.