以α，ω－二羟基聚二甲基硅氧烷（107硅橡胶）、交联剂、催化剂、偶联剂为原料，制得脱醇型单组分室温硫化（RTV－1）硅橡胶。考察了107硅橡胶的黏度、交联剂用量、催化剂种类、偶联剂类型和用量对脱醇型RTV－1硅橡胶硫化速度的影响。结果表明，当107硅橡胶的黏度为60000 mPa· s，交联剂用量为4％，1％的钛酸酯配合物1作为催化剂，偶联剂KH－792的用量为0.3％时，制得的脱醇型RTV－1硅橡胶具有较好的硫化速度，表干时间为15 min，8 h硫化深度为1.32 mm，24 h硫化深度为2.24 mm。
이α，ω－이간기취이갑기규양완（107규상효）、교련제、최화제、우련제위원료，제득탈순형단조분실온류화（RTV－1）규상효。고찰료107규상효적점도、교련제용량、최화제충류、우련제류형화용량대탈순형RTV－1규상효류화속도적영향。결과표명，당107규상효적점도위60000 mPa· s，교련제용량위4％，1％적태산지배합물1작위최화제，우련제KH－792적용량위0.3％시，제득적탈순형RTV－1규상효구유교호적류화속도，표간시간위15 min，8 h류화심도위1.32 mm，24 h류화심도위2.24 mm。
The dealcoholized one -component room temperature vulcanized ( RTV -1 ) silicone rubber was prepared by α,ω-dihydroxy polydimethylsiloxane ( 107 silicone rubber ) , crosslinking agent , catalyst and coupling agent .The factors which affected the curing rate of dealcoholized RTV -1 silicone rubber were stud-ied, including the viscosity of 107 rubber, the content of cross linking agent , the type and content of coupling agent and the type of catalyst .Results showed that the dealcoholized RTV -1 silicone rubber had a high cu-ring rate prepared with 60 000 mPa· s of 107 rubber , 4%crosslinking agent , 1%titanate chelate 1 and 0 .3%KH-792.The tack-free time is 15min, curing depth for 8 h and 24 h was 1.32mm and 2.24mm, respec-tively .