氢脆是电镀过程中经常出现的一种破坏现象，严重危害镀层质量。特别是氢脆发生不容易检测，可能造成材料的突然断裂，所以对氢脆形成机理的研究更为重要。本文对氢脆产生的原因进行论述，重点研究了第二类氢脆的产生机理，以便提出更好的预防措施和控制方法。
경취시전도과정중경상출현적일충파배현상，엄중위해도층질량。특별시경취발생불용역검측，가능조성재료적돌연단렬，소이대경취형성궤리적연구경위중요。본문대경취산생적원인진행논술，중점연구료제이류경취적산생궤리，이편제출경호적예방조시화공제방법。
Hydrogen embrittlement is a damage phenomenon often appears in the process of electroplating. Hydrogen embrittlement is not easy to detect, it may cause material suddenly rupture, so the study of hydrogen embrittlement mechanism is very important. This paper discusses the main causes of hydrogen embrittlement, focus to study the mechanism of the second category of hydrogen embrittlement to better put forward the prevention and control methods.