材料导报
材料導報
재료도보
MATERIALS REVIEW
2015年
16期
52-57
,共6页
易新龙%冯安妮%邵文尧%肖宗源
易新龍%馮安妮%邵文堯%肖宗源
역신룡%풍안니%소문요%초종원
硼改性酚醛树脂%红外光谱%热性能%力学性能%模塑料
硼改性酚醛樹脂%紅外光譜%熱性能%力學性能%模塑料
붕개성분철수지%홍외광보%열성능%역학성능%모소료
boron modified phenolic resin%infrared spectroscopy%thermal properties%mechanic performance%molding plastics
研究了硼酸加入量对所合成硼改性酚醛树脂性能的影响。通过红外光谱和热重等分析手段对硼改性酚醛树脂的结构和热性能进行表征,分别考察其在氮气和空气氛围下的残炭率,获知当苯酚、甲醛和硼酸之间的物质的量比为1∶1.4∶0.4时,硼改性酚醛树脂的残炭率最高,分别为67.82%和10.92%。此外,以硼改性酚醛树脂为基体树脂制备模塑料并考察其拉伸强度、弯曲强度和抗冲击强度等力学性能。综合考虑以上热性能和力学性能,确定苯酚、甲醛和硼酸之间的最佳物质的量比为1∶1.4∶0.3。最后,研究了添加不同种类和不同含量的填料对酚醛模塑料力学性能的影响。研究结果表明:以短玻璃纤维为填料时,酚醛模塑料的力学性能优于木粉和长玻璃纤维混合物填料;若使用木粉和长玻璃纤维混合物填料,当木粉与长玻璃纤维的质量比为1∶3时,酚醛模塑料的力学性能最佳。
研究瞭硼痠加入量對所閤成硼改性酚醛樹脂性能的影響。通過紅外光譜和熱重等分析手段對硼改性酚醛樹脂的結構和熱性能進行錶徵,分彆攷察其在氮氣和空氣氛圍下的殘炭率,穫知噹苯酚、甲醛和硼痠之間的物質的量比為1∶1.4∶0.4時,硼改性酚醛樹脂的殘炭率最高,分彆為67.82%和10.92%。此外,以硼改性酚醛樹脂為基體樹脂製備模塑料併攷察其拉伸彊度、彎麯彊度和抗遲擊彊度等力學性能。綜閤攷慮以上熱性能和力學性能,確定苯酚、甲醛和硼痠之間的最佳物質的量比為1∶1.4∶0.3。最後,研究瞭添加不同種類和不同含量的填料對酚醛模塑料力學性能的影響。研究結果錶明:以短玻璃纖維為填料時,酚醛模塑料的力學性能優于木粉和長玻璃纖維混閤物填料;若使用木粉和長玻璃纖維混閤物填料,噹木粉與長玻璃纖維的質量比為1∶3時,酚醛模塑料的力學性能最佳。
연구료붕산가입량대소합성붕개성분철수지성능적영향。통과홍외광보화열중등분석수단대붕개성분철수지적결구화열성능진행표정,분별고찰기재담기화공기분위하적잔탄솔,획지당분분、갑철화붕산지간적물질적량비위1∶1.4∶0.4시,붕개성분철수지적잔탄솔최고,분별위67.82%화10.92%。차외,이붕개성분철수지위기체수지제비모소료병고찰기랍신강도、만곡강도화항충격강도등역학성능。종합고필이상열성능화역학성능,학정분분、갑철화붕산지간적최가물질적량비위1∶1.4∶0.3。최후,연구료첨가불동충류화불동함량적전료대분철모소료역학성능적영향。연구결과표명:이단파리섬유위전료시,분철모소료적역학성능우우목분화장파리섬유혼합물전료;약사용목분화장파리섬유혼합물전료,당목분여장파리섬유적질량비위1∶3시,분철모소료적역학성능최가。
The effects of boracic acid dosage on the properties of modified phenolic resin were studied.The structure and thermal property of boron modified phenolic resin were characterized with infrared spectroscopy (IR) and thermogravimetric analyzer (TGA),respectively.It was shown that the residual carbon rate of the boron modified phenolic resin was 10.92% and 67.82%,respectively under the air and nitrogen conditions,when n(phenol)∶n(for-maldehyde)∶n(boron acid)= 1 ∶ 1.4 ∶ 0.4.Also,the mechanic properties,such as tensile,flexural and impact strength of the molding plastics prepared by boron modified phenolic resin were investigated.With the consideration of thermal and mechanic properties,the optimum molar ratio was obtained as n(phenol)∶n(formaldehyde)∶n(boracic acid)=1∶1.4∶0.3.Besides,the effects of filler kind and content for the molding plastics on its mechanic properties were investigated.It was shown that short glass fiber as filler was much better than long glass fiber and wood pow-der,and when wood powder and long glass fiber were used as the mixing filler,the optimum mass ratio of long glass fiber to wood powder was 3∶1.