CAJ | 학술논문

To realize the comprehensive utilization of coal-fired industrial solid wastes, a novel high-strength board was prepared from cal-cium silicate slag, fly ash, and flue gas desulfurization (FGD) gypsum. The changes in mineral phases, chemical structure, and morphology during hydration were investigated by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and scanning electron mi-croscopy (SEM). A traditional board made from quartz and lime was prepared as a reference. The novel board not only consumes a lot of solid wastes, but also meets the strength requirement of the class-five calcium silicate board according to the Chinese Standard JC/T 564.2—2008. Microanalysis showed that hydrated calcium silicate gel (C?S?H(I)), ettringite, tobermorite, and xonotlite were successivelygenerated in the novel board by synergistic hydration of the mixed solid wastes. The board strength was improved by the formation of tobermorite and xonotlite but decreased by unhydrated quartz. It was demonstrated that quartz was not completely hydrated in the traditional board. As a re-sult, the flexural strength of the traditional board was much lower than that of the novel board.