广东工业大学学报
廣東工業大學學報
엄동공업대학학보
Journal of Guangdong University of Technology
2015年
3期
133-136,146
,共5页
李倩%袁鸽成%骆志捷%邓南林%张普
李倩%袁鴿成%駱誌捷%鄧南林%張普
리천%원합성%락지첩%산남림%장보
溶胶-凝胶%熔融-淬火%Bi-Si-B-O玻璃体系%玻璃结构
溶膠-凝膠%鎔融-淬火%Bi-Si-B-O玻璃體繫%玻璃結構
용효-응효%용융-쉬화%Bi-Si-B-O파리체계%파리결구
sol-gel%melt-quenching%Bi-Si-B-O glassy powder%glass structure
采用溶胶-凝胶法( Sol-Gel)和熔融-淬火法分别制备了Bi-Si-B-Zn-Al-O系玻璃粉体,运用XRD、SEM、EMAX、IR、DSC/TG等手段对粉体进行了表征,并初步探讨了同体系不同制备方法下两种玻璃粉体的微观结构的异同.结果表明,两种玻璃粉体均呈玻璃态,溶胶-凝胶粉体颗粒较易破碎,球磨12 h后可得到1~10μm范围的颗粒,其元素含量与实验设计比例较为接近;两种粉体玻璃网络结构相似,主要以[ BiO3]三角体、[ SiO4]四面体、[ BO4]四面体构成基本网络骨架;熔融-淬火玻璃结构中[ SiO4]四面体趋向于架状,使得粉体结构更加稳定,玻璃转化温度略高于溶胶-凝胶玻璃且均小于600℃.
採用溶膠-凝膠法( Sol-Gel)和鎔融-淬火法分彆製備瞭Bi-Si-B-Zn-Al-O繫玻璃粉體,運用XRD、SEM、EMAX、IR、DSC/TG等手段對粉體進行瞭錶徵,併初步探討瞭同體繫不同製備方法下兩種玻璃粉體的微觀結構的異同.結果錶明,兩種玻璃粉體均呈玻璃態,溶膠-凝膠粉體顆粒較易破碎,毬磨12 h後可得到1~10μm範圍的顆粒,其元素含量與實驗設計比例較為接近;兩種粉體玻璃網絡結構相似,主要以[ BiO3]三角體、[ SiO4]四麵體、[ BO4]四麵體構成基本網絡骨架;鎔融-淬火玻璃結構中[ SiO4]四麵體趨嚮于架狀,使得粉體結構更加穩定,玻璃轉化溫度略高于溶膠-凝膠玻璃且均小于600℃.
채용용효-응효법( Sol-Gel)화용융-쉬화법분별제비료Bi-Si-B-Zn-Al-O계파리분체,운용XRD、SEM、EMAX、IR、DSC/TG등수단대분체진행료표정,병초보탐토료동체계불동제비방법하량충파리분체적미관결구적이동.결과표명,량충파리분체균정파리태,용효-응효분체과립교역파쇄,구마12 h후가득도1~10μm범위적과립,기원소함량여실험설계비례교위접근;량충분체파리망락결구상사,주요이[ BiO3]삼각체、[ SiO4]사면체、[ BO4]사면체구성기본망락골가;용융-쉬화파리결구중[ SiO4]사면체추향우가상,사득분체결구경가은정,파리전화온도략고우용효-응효파리차균소우600℃.
The glassy powder of the Bi-Si-B-Zn-Al-O system is prepared by sol-gel and melt-quenching methods.The powder is characterized by means of XRD, SEM, EMAX, IR, DSC/TG, and the similari-ties and differences of the microstructure under different preparations are explored roughly.The results show that both of the two have amorphous structure.Compared with melt-quenching one, the glassy pow-der of sol-gel method can be broken easily , and the particle size in the range of 1~10μm is obtained af-ter ball milling, the element of which is relatively close to the designed.The network structures of the two kinds of glassy powder are similar, the [ BiO3 ] triangular, [ SiO4 ] tetrahedron and [ BO4 ] tetrahedron forming the glass′s basic network, but the melt-quenching glassy structure in [ SiO4 ] tetrahedron tends to be like framework, which makes the powder structure more stable, the glass transition temperature slight-ly higher than the sol-gel glass, and both of them are less than 600℃.