黄君%邵智猛%任印宝%赵情儿%洪佳丹%王倩%邓德刚%余华%徐时清
黃君%邵智猛%任印寶%趙情兒%洪佳丹%王倩%鄧德剛%餘華%徐時清
황군%소지맹%임인보%조정인%홍가단%왕천%산덕강%여화%서시청
荧光粉%BaKBP2O8:Eu2+%蓝光发射
熒光粉%BaKBP2O8:Eu2+%藍光髮射
형광분%BaKBP2O8:Eu2+%람광발사
phosphors%BaKBP2 O8:Eu2+%blue-emitting
通过高温固相法成功合成了一种新型蓝光荧光粉BaKBP2 O8:Eu2+,分别用XRD和荧光光谱表征了其结构与光学性能。结果表明,Eu2+的引入并没有显著改变其四方相的晶体结构。样品的激发光谱(监测波长为443 nm)是由主晶格吸收的307 nm吸收肩与Eu2+离子4f7-4f65d跃迁的346 nm主峰组成。在紫光激发下,样品的发射光谱为蓝色。当Eu2+离子摩尔分数为0.03时,样品的发射强度达到最大值。然而,随着Eu2+浓度的进一步增加,由于浓度猝灭机制,其发射强度开始降低。在超过370 K的温度下,荧光粉样品的相对发光强度仍然超过50%。 BaKBP2 O8:Eu2+的色坐标为(0.1766,0.1681)。
通過高溫固相法成功閤成瞭一種新型藍光熒光粉BaKBP2 O8:Eu2+,分彆用XRD和熒光光譜錶徵瞭其結構與光學性能。結果錶明,Eu2+的引入併沒有顯著改變其四方相的晶體結構。樣品的激髮光譜(鑑測波長為443 nm)是由主晶格吸收的307 nm吸收肩與Eu2+離子4f7-4f65d躍遷的346 nm主峰組成。在紫光激髮下,樣品的髮射光譜為藍色。噹Eu2+離子摩爾分數為0.03時,樣品的髮射彊度達到最大值。然而,隨著Eu2+濃度的進一步增加,由于濃度猝滅機製,其髮射彊度開始降低。在超過370 K的溫度下,熒光粉樣品的相對髮光彊度仍然超過50%。 BaKBP2 O8:Eu2+的色坐標為(0.1766,0.1681)。
통과고온고상법성공합성료일충신형람광형광분BaKBP2 O8:Eu2+,분별용XRD화형광광보표정료기결구여광학성능。결과표명,Eu2+적인입병몰유현저개변기사방상적정체결구。양품적격발광보(감측파장위443 nm)시유주정격흡수적307 nm흡수견여Eu2+리자4f7-4f65d약천적346 nm주봉조성。재자광격발하,양품적발사광보위람색。당Eu2+리자마이분수위0.03시,양품적발사강도체도최대치。연이,수착Eu2+농도적진일보증가,유우농도졸멸궤제,기발사강도개시강저。재초과370 K적온도하,형광분양품적상대발광강도잉연초과50%。 BaKBP2 O8:Eu2+적색좌표위(0.1766,0.1681)。
Novel efficient blue phosphors Ba1-x KBP2 O8:xEu2+ were successfully synthesized by high-temperature solid state reaction. The structure and luminescence properties were characterized systematically by XRD and fluores-cence spectra, respectively. The results show that Eu2+doping does not produce significant changes for the crystal structure which remains pure tetragonal. Excitation spectrum ( monitoring wavelength is 443 nm) is composed of the acromion at 307 nm due to host absorption, and the main peak at 346 nm due to 4f7-4f65d transition Eu2+ ions. Un-der violet light excitation, the samples emit blue light. When the mole fraction of Eu2+ is 0. 03, the emission spec-trum has a maximum intensity. However, with further increase of the concentration of Eu2+, the emission spectrum intensity decreases, as a result of concentration quenching. At temperatures over 370 K, the intensity of the phos-phors is still more than 50%. The CIE chromaticity coordinate of BaKBP2O8:Eu2+ is (0. 176 6, 0. 168 1).