本文主要介绍了铝合金牺牲阳极的开发现状,分析了干湿交替环境铝合金牺牲阳极性能下降的原因,并综述了目前我国干湿交替环境下铝合金牺牲阳极的研发现状.
本文主要介紹瞭鋁閤金犧牲暘極的開髮現狀,分析瞭榦濕交替環境鋁閤金犧牲暘極性能下降的原因,併綜述瞭目前我國榦濕交替環境下鋁閤金犧牲暘極的研髮現狀.
본문주요개소료려합금희생양겁적개발현상,분석료간습교체배경려합금희생양겁성능하강적원인,병종술료목전아국간습교체배경하려합금희생양겁적연발현상.
In this paper, development status of Al-alloy sacrificial anode was referred and reason of performance reduction of Al-alloy sacrificial anode used in the dry-wet alternate environment was analyzed, meanwhile, research and development status of Al-alloy sacrificial anode used in the dry-wet alternate environment was summarized.