copper mold suction casting%nanocomposite bulk magnets%microstructure%annealing treatment%magnetic properties%rare earths
The bulk nanocomposite magnets of Nd9Fe81–xTi4C2Nb4Bx (x=11, 13, 15) in sheet form with the thickness of 0.7 mm were prepared by copper mold suction casting and subsequently annealing. The microstructure evolution and magnetic properties of bulk magnets were studied. It was shown that the as-cast microstructure of bulk alloys were composed of Nd2Fe14B,α-Fe, Fe3B crystalline phases and an amorphous matrix, and that the glass formability of alloy was improved with increasing the B content. The DSC analy-sis showed that the as-cast bulk alloys had the crystallization behavior of a two-step process. After annealing at the temperatures which was 40–63 K higher than their onset temperatures of the second exothermic peak, Nd9Fe81–xTi4C2Nb4Bx (x=11, 13, 15) bulk al-loys obtained a finely mixed structure which were composed of Nd2Fe14B,α-Fe, Fe3B, (Nb,Ti)C crystalline phases and a residual amorphous phase, whose magnetic properties were significantly enhanced. For the bulk magnets of Nd9Fe81–xTi4C2Nb4Bx (x=11, 13, 15), the optimal magnetic properties ofBr=0.63 T,iHc=155.1 kA/m, (BH)max=18.73 kJ/m3 could be achieved whenx=13 after anneal-ing at 983 K for 10 min.