利用超音速火焰喷涂制备微米WC-12Co、纳米改性WC-12Co和CeO2改性WC-12Co涂层,通过对涂层微观组织、硬度和腐蚀磨损性能进行分析,研究CeO2对WC-12Co涂层腐蚀磨损性能的影响.结果表明:CeO2的加入可以降低涂层的孔隙率,抑制晶粒长大,提高涂层硬度,涂层的耐腐蚀磨损性能也得到提高.在腐蚀磨损中,材料的流失主要是由于腐蚀磨损的交互作用引起的,交互作用造成的失重约占总失重量的90%~99%.同时,在腐蚀和磨损的交互作用中,腐蚀对磨损的加速量远大于磨损对腐蚀的加速量,磨损分量在整个腐蚀磨损过程中占主导地位,提高WC-Co涂层的耐腐蚀磨损性能的关键在于提高涂层的耐磨损性能.
이용초음속화염분도제비미미WC-12Co、납미개성WC-12Co화CeO2개성WC-12Co도층,통과대도층미관조직、경도화부식마손성능진행분석,연구CeO2대WC-12Co도층부식마손성능적영향.결과표명:CeO2적가입가이강저도층적공극솔,억제정립장대,제고도층경도,도층적내부식마손성능야득도제고.재부식마손중,재료적류실주요시유우부식마손적교호작용인기적,교호작용조성적실중약점총실중량적90%~99%.동시,재부식화마손적교호작용중,부식대마손적가속량원대우마손대부식적가속량,마손분량재정개부식마손과정중점주도지위,제고WC-Co도층적내부식마손성능적관건재우제고도층적내마손성능.
The micro WC-12Co, nano modified WC-12Co and CeO2 modified WC-12Co coatings were prepared by high velocity oxy-fuel thermal spray (HVOF) method. The microstructure, hardness and corrosion-wear resistance of the coatings were tested to study the effects of CeO2 on the corrosion-wear properties of WC-12Co coatings. The results showed that the addition of CeO2 can decrease the porosity of the coating, inhibit the grain growth and increase the coating hardness. It also can improve the corrosion-wear properties of the coating. In the corrosion-wear process, the weight loss caused by the interaction of corrosion-wear occupied about 90%~99% in the total weight loss. The corrosion accerating wear effect was far more than the wear accerating corrosion effect in the interaction of corrosion and wear, the wear component dominated the whole corrosion wear process. So the key to improve the corrosion-wear properties of WC-12Co coating was to improve the wear resistanceof the coating.