胶原蛋白%F-90%超细纤维合成革基布%卫生性能
膠原蛋白%F-90%超細纖維閤成革基佈%衛生性能
효원단백%F-90%초세섬유합성혁기포%위생성능
collagen%F-90%microfiber synthetic leather base%sanitary properties%improvement
采用硫酸水解超细纤维合成革基布,暴露基布的活性基团;以鞣剂F-90作为交联剂,将胶原蛋白接枝到超细纤维合成革基布上,以期改善基布的卫生性能。结果表明:最佳改性工艺条件为:胶原蛋白用量15%、F-90用量6%、改性温度45℃、时间4 h、体系pH 7.0;该条件下处理后,基布的羧基含量增加188.82%,氨基含量增加124.19%,透水汽性提高65.15%,吸水性提高58.04%,且其抗张强度、断裂伸长率和撕裂强度均有所提高。采用FI-IR、XPS、SEM和接触角分别对改性前后基布进行表征,结果显示:胶原蛋白能够成功交联改性到基布上,改性后基布表面的活性基团增加,纤维松散程度增大,润湿性提高。
採用硫痠水解超細纖維閤成革基佈,暴露基佈的活性基糰;以鞣劑F-90作為交聯劑,將膠原蛋白接枝到超細纖維閤成革基佈上,以期改善基佈的衛生性能。結果錶明:最佳改性工藝條件為:膠原蛋白用量15%、F-90用量6%、改性溫度45℃、時間4 h、體繫pH 7.0;該條件下處理後,基佈的羧基含量增加188.82%,氨基含量增加124.19%,透水汽性提高65.15%,吸水性提高58.04%,且其抗張彊度、斷裂伸長率和撕裂彊度均有所提高。採用FI-IR、XPS、SEM和接觸角分彆對改性前後基佈進行錶徵,結果顯示:膠原蛋白能夠成功交聯改性到基佈上,改性後基佈錶麵的活性基糰增加,纖維鬆散程度增大,潤濕性提高。
채용류산수해초세섬유합성혁기포,폭로기포적활성기단;이유제F-90작위교련제,장효원단백접지도초세섬유합성혁기포상,이기개선기포적위생성능。결과표명:최가개성공예조건위:효원단백용량15%、F-90용량6%、개성온도45℃、시간4 h、체계pH 7.0;해조건하처리후,기포적최기함량증가188.82%,안기함량증가124.19%,투수기성제고65.15%,흡수성제고58.04%,차기항장강도、단렬신장솔화시렬강도균유소제고。채용FI-IR、XPS、SEM화접촉각분별대개성전후기포진행표정,결과현시:효원단백능구성공교련개성도기포상,개성후기포표면적활성기단증가,섬유송산정도증대,윤습성제고。
Microfiber synthetic leather base were pretreated with sulfuric acid to expose active groups on the surface, which was then modified with collagen using F-90 as a cross-linking agent to enhance sanitary properties. The optimized conditions were found as: collagen dosage 15%, F-90 dosage 6%, temperature 45℃, time 4 h and pH 7.0. The modified samples show an increase of carboxyl and amino group by 188.82% and 124.19%, respectively. Water vapor permeability is improved by 65.15% and hygroscopicity was improved by 58.04%. Tensile strength, elongation at break, and tearing strength of the sample were also found enhanced after modification. Furthermore, FI-IR, XPS, SEM and contact angle results show that collagen is successful attached on the surface with active groups increased. The fiber looseness degree of the modified sample is increased and its hygroscopicity is enhanced.