炭黑G660%工业车辆轮胎%胎侧胶%耐屈挠性能%生热
炭黑G660%工業車輛輪胎%胎側膠%耐屈撓性能%生熱
탄흑G660%공업차량륜태%태측효%내굴뇨성능%생열
carbon black G660%industrial vehicle tire%sidewall compound%lfex resistance%heat build-up
研究炭黑G660在工业车辆轮胎胎侧胶中的应用。结果表明，与炭黑N660胶料相比，炭黑G660胶料的300%定伸应力、拉伸强度和撕裂强度相差不大，拉断伸长率较大，生热较低，耐屈挠性能较好，工艺性能满足生产要求，成本降低，成品轮胎物理性能相当。
研究炭黑G660在工業車輛輪胎胎側膠中的應用。結果錶明，與炭黑N660膠料相比，炭黑G660膠料的300%定伸應力、拉伸彊度和撕裂彊度相差不大，拉斷伸長率較大，生熱較低，耐屈撓性能較好，工藝性能滿足生產要求，成本降低，成品輪胎物理性能相噹。
연구탄흑G660재공업차량륜태태측효중적응용。결과표명，여탄흑N660효료상비，탄흑G660효료적300%정신응력、랍신강도화시렬강도상차불대，랍단신장솔교대，생열교저，내굴뇨성능교호，공예성능만족생산요구，성본강저，성품륜태물이성능상당。
In this study, carbon black G660 was applied in the sidewall compound of industrial vehicle tire. The results showed that, compared with carbon black N660 filled compound, the tensile modulus at 300%elongation, tensile strength and tear strength of G660 iflled compound were similar, the elongation at break was larger, heat build-up was lower, and lfex resistance was better. The processing property of the compound iflled with G660 met the production requirements and the cost was reduced. The ifnished tire with G660 iflled sidewall showed similar physical properties as that with N660 iflled sidewall.