CDQ boiler%Tube burst%Secondary superheater%Sulfur corrosion
通过对已损坏的二次过热器管进行扫描电镜观察及能谱分析,认为高温硫腐蚀是造成干熄焦锅炉二次过热器管壁损坏进而引起锅炉爆管的主要原因,改进后没有再发生爆管事故.
通過對已損壞的二次過熱器管進行掃描電鏡觀察及能譜分析,認為高溫硫腐蝕是造成榦熄焦鍋爐二次過熱器管壁損壞進而引起鍋爐爆管的主要原因,改進後沒有再髮生爆管事故.
통과대이손배적이차과열기관진행소묘전경관찰급능보분석,인위고온류부식시조성간식초과로이차과열기관벽손배진이인기과로폭관적주요원인,개진후몰유재발생폭관사고.
This paper analyzes the broken tubes of secondary superheater by Scanning Electron Microscope ( SEM ) and Energy Dispersive X-Ray Spectroscopy ( EDS ) and found that the high temperature sulfur corrosion is the main reason for the tube damage and further tube burst. After corresponding improvement, there is no more tube burst accident.